SM ISO690:2012 FORSH, Ekaterina, MARTYSHOV, M., FORSH, Pavel, KASHKAROV, P.. Optical and photoelectrical features in nanocrystalline indium oxide. In: Microelectronics and Computer Science: The 5th International Conference, Ed. 8, 22-25 octombrie 2014, Chisinau. Chișinău, Republica Moldova: Universitatea Tehnică a Moldovei, 2014, Ediția 8, pp. 72-74. ISBN 978-9975-45-329-5.. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Microelectronics and Computer Science Ediția 8, 2014 |
||||||
Conferința "Microelectronics and Computer Science" 8, Chisinau, Moldova, 22-25 octombrie 2014 | ||||||
|
||||||
Pag. 72-74 | ||||||
|
||||||
Descarcă PDF | ||||||
Rezumat | ||||||
Spectral dependencies of absorption coefficient and persistent photoconductivity in nanocrystalline indium oxide (In2O3) are studied. Nanostructured In2O3 samples with various nanocrystals size are prepared by sol-gel method and characterized using various techniques. The mean nanocrystals size varies from 7–8 nm to 39–41 nm depending on the preparation conditions. Structural characterization of the In2O3 samples is performed by means of transmission electron microscopy and X-ray diffraction. The analysis of ultraviolet – visible absorption spectroscopy shows that nanostructuring leads to the change in optical band gap: optical band gap of the In2O3 samples (with an average nanocrystal size from 7 to 41 nm) is equal to 2.8 eV. We find out the correlation between spectral dependence of photoconductivity and optical properties of nanocrystalline In2O3: sharp increase in photoconductivity was observed to begin at 2.8 eV energy equal to the optical bandgap in the In2O3 samples, and reached its maximum at energies of 3.2–3.3 eV. |
||||||
Cuvinte-cheie absorption, nanocrystalline indium oxide, Persistent Photoconductivity, ultraviolet – visible absorption spectroscopy. |
||||||
|