Application of nano-oxide films on the surfaces of parts made of titanium alloys in order to increase their corrosion resistance
Închide
Articolul precedent
Articolul urmator
594 0
SM ISO690:2012
TOPALĂ, Pavel, OJEGOV, Alexandr, STOICEV, Petru. Application of nano-oxide films on the surfaces of parts made of titanium alloys in order to increase their corrosion resistance. In: Nanotechnologies and Biomedical Engineering, Ed. 3, 23-26 septembrie 2015, Chișinău. Springer, 2015, Editia 3, p. 64.
EXPORT metadate:
Google Scholar
Crossref
CERIF

DataCite
Dublin Core
Nanotechnologies and Biomedical Engineering
Editia 3, 2015
Conferința "International Conference on Nanotechnologies and Biomedical Engineering"
3, Chișinău, Moldova, 23-26 septembrie 2015

Application of nano-oxide films on the surfaces of parts made of titanium alloys in order to increase their corrosion resistance


Pag. 64-64

Topală Pavel1, Ojegov Alexandr1, Stoicev Petru2
 
1 "Alecu Russo" State University of Balti,
2 Technical University of Moldova
 
Disponibil în IBN: 9 aprilie 2019


Rezumat

The paper presents the results of nano-scale oxide films formation on sample surfaces made of titanium alloys that is material with a wide application in medicine and biomedicine. It was demonstrated that by the action of the plasma formed under ordinary conditions in the air media their surface is enriched with oxygen and nitrogen elements, the first substantially increases the corrosion resistance, and the other – the mechanical strength of the processed parts. The increase of corrosion resistance by at least 10 times in chemically active environments (30% aqueous solution of H2SO4 at the temperature of 80 °C) was observed for the processed titanium parts’ surfaces.