SM ISO690:2012 GUTSUL, Tatiana, NIKORICH, Andrey V., TODOSICIUC, Alexandr. Solvothermal synthesis of lead telluride micro- and nanocrystals. In: Proceedings of the International Semiconductor Conference: CAS, Ed. 34, 17-19 octombrie 2011, Sinaia. New Jersey: Institute of Electrical and Electronics Engineers Inc., 2011, Vol. 2, pp. 257-260. ISBN 978-161284171-7. DOI: https://doi.org/10.1109/SMICND.2011.6095785 |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Proceedings of the International Semiconductor Conference Vol. 2, 2011 |
|||||||
Conferința " International Semiconductor Conference" 34, Sinaia, Romania, 17-19 octombrie 2011 | |||||||
|
|||||||
DOI:https://doi.org/10.1109/SMICND.2011.6095785 | |||||||
Pag. 257-260 | |||||||
|
|||||||
Descarcă PDF | |||||||
Rezumat | |||||||
Single-crystalline nanoparticles and rod-shaped lead telluride microparticles were obtained using solvothermal synthesis. It is shown that the reaction temperature, time of the synthesis, and precursor molar ratio make it possible to tune the shape and size of nanocrystals. X-Ray powder diffraction with transmission electron microscopy was used to confirm the crystallinity and morphology of nanoparticles obtained. The temperature dependence of the electric conductivity was also measured, and its values are close to values of bulk PbTe. |
|||||||
Cuvinte-cheie Crystallinities, Lead telluride, Micro-particles, molar ratio, PbTe, Reaction temperature, Rod-shaped, Shape and size, Single-crystalline, Solvothermal synthesis, Temperature dependence |
|||||||
|