Articolul precedent |
Articolul urmator |
696 3 |
Ultima descărcare din IBN: 2020-05-04 14:21 |
SM ISO690:2012 TSYNTSARU, Natalia, KAVAS, Berkay, CELIS, Jean-Pierre. Synthesis of AAO nanotemplate and its properties. In: Nanotechnologies and Biomedical Engineering, Ed. 1, 7-8 iulie 2011, Chișinău. Technical University of Moldova, 2011, Editia 1, pp. 75-79. ISBN 978-9975-66-239-0.. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Nanotechnologies and Biomedical Engineering Editia 1, 2011 |
||||||
Conferința "International Conference on Nanotechnologies and Biomedical Engineering" 1, Chișinău, Moldova, 7-8 iulie 2011 | ||||||
|
||||||
Pag. 75-79 | ||||||
|
||||||
Descarcă PDF | ||||||
Rezumat | ||||||
The objective of this study is to synthesize and to characterize anodized aluminium oxide (AAO) nano-templates suited for large area device applications. The wear performance and the mechanical properties of well-ordered nanoporous AAO obtained after a two step anodizing process in sulphuric acid were investigated. Pores with different aspect ratios were obtained at cell voltages of 15 V and 21V. Ppore diameters of ~16 nm and ~ 27 nm were noticed. The mechanical behaviour of such anodized aluminium oxides (AAO) was determined by nanoindentation at 2 -200mN normal loads. The tribological behaviour of these nano-templates was studied under reciprocating (ball on flat) sliding against alumina counter-balls. The dependence of the properties of AAO-templates on the small pore diameter is discussed |
||||||
Cuvinte-cheie anodized aluminium oxide, friction and wear, hardness, pore diameter |
||||||
|
Dublin Core Export
<?xml version='1.0' encoding='utf-8'?> <oai_dc:dc xmlns:dc='http://purl.org/dc/elements/1.1/' xmlns:oai_dc='http://www.openarchives.org/OAI/2.0/oai_dc/' xmlns:xsi='http://www.w3.org/2001/XMLSchema-instance' xsi:schemaLocation='http://www.openarchives.org/OAI/2.0/oai_dc/ http://www.openarchives.org/OAI/2.0/oai_dc.xsd'> <dc:creator>Ţînţaru, N.I.</dc:creator> <dc:creator>Kavas, B.</dc:creator> <dc:creator>Celis, J.</dc:creator> <dc:date>2011</dc:date> <dc:description xml:lang='en'><p>The objective of this study is to synthesize and to characterize anodized aluminium oxide (AAO) nano-templates suited for large area device applications. The wear performance and the mechanical properties of well-ordered nanoporous AAO obtained after a two step anodizing process in sulphuric acid were investigated. Pores with different aspect ratios were obtained at cell voltages of 15 V and 21V. Ppore diameters of ~16 nm and ~ 27 nm were noticed. The mechanical behaviour of such anodized aluminium oxides (AAO) was determined by nanoindentation at 2 -200mN normal loads. The tribological behaviour of these nano-templates was studied under reciprocating (ball on flat) sliding against alumina counter-balls. The dependence of the properties of AAO-templates on the small pore diameter is discussed</p></dc:description> <dc:source>Nanotechnologies and Biomedical Engineering (Editia 1) 75-79</dc:source> <dc:subject>anodized aluminium oxide</dc:subject> <dc:subject>friction and wear</dc:subject> <dc:subject>hardness</dc:subject> <dc:subject>pore diameter</dc:subject> <dc:title>Synthesis of AAO nanotemplate and its properties</dc:title> <dc:type>info:eu-repo/semantics/article</dc:type> </oai_dc:dc>