 SM ISO690:2012ГАМБУРГ , Ю., ЗАХАРОВ, Е.. Электроосаждение тройных сплавов Fe-W-H. In: Электронная обработка материалов, 2018, nr. 6(54), pp. 1-8. ISSN 0013-5739. DOI: https://doi.org/10.5281/zenodo.1968647 |
| EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
 Электронная обработка материалов |
||||||
| Numărul 6(54) / 2018 / ISSN 0013-5739 /ISSNe 2345-1718 | ||||||
|
||||||
| DOI:https://doi.org/10.5281/zenodo.1968647 | ||||||
| CZU: 541.138 | ||||||
| Pag. 1-8 | ||||||
|
||||||
 Descarcă PDF |
||||||
| Rezumat | ||||||
Изучены процесс электрохимического осаждения, а также структура и свойства сплавов Fe-W. Сплавы, полученные при низкой плотности тока, представляют собой кристаллические пересыщенные твердые растворы W в Fe и являются магнитными. Более высокие плотности тока приводят к получению аморфных немагнитных сплавов того же состава. После обработки при 500–600°С как аморфные, так и кристаллические сплавы переходили в более равновесную бинарную систему, содержащую твердый раствор W в Fe и интерметаллическое соединение. Концентрация оставшегося вольфрама в твердом растворе была много выше равновесной растворимости. В осадки включалось значительное количество водорода. Фактически полученные осадки могут быть квалифицированы как тройные сплавы Fe-W-H. Включенный водород играет решающую роль в переходе от кристаллического состояния, типичного для образцов, полученных при низкой плотности тока, к аморфным или нанокристаллическим осадкам, образованным при более высокой плотности тока |
||||||
| Cuvinte-cheie электроосаждение, структура, вольфрам, сплавы, аморфизация. |
||||||
|
Cerif XML Export
<?xml version='1.0' encoding='utf-8'?> <CERIF xmlns='urn:xmlns:org:eurocris:cerif-1.5-1' xsi:schemaLocation='urn:xmlns:org:eurocris:cerif-1.5-1 http://www.eurocris.org/Uploads/Web%20pages/CERIF-1.5/CERIF_1.5_1.xsd' xmlns:xsi='http://www.w3.org/2001/XMLSchema-instance' release='1.5' date='2012-10-07' sourceDatabase='Output Profile'> <cfResPubl> <cfResPublId>ibn-ResPubl-69726</cfResPublId> <cfResPublDate>2018-12-20</cfResPublDate> <cfVol>54</cfVol> <cfIssue>6</cfIssue> <cfStartPage>1</cfStartPage> <cfISSN>0013-5739</cfISSN> <cfURI>https://ibn.idsi.md/ro/vizualizare_articol/69726</cfURI> <cfTitle cfLangCode='RU' cfTrans='o'>Электроосаждение тройных сплавов Fe-W-H</cfTitle> <cfKeyw cfLangCode='RU' cfTrans='o'>электроосаждение; структура; сплавы; вольфрам; аморфизация.</cfKeyw> <cfAbstr cfLangCode='RU' cfTrans='o'><p>Изучены процесс электрохимического осаждения, а также структура и свойства сплавов Fe-W. Сплавы, полученные при низкой плотности тока, представляют собой кристаллические пересыщенные твердые растворы W в Fe и являются магнитными. Более высокие плотности тока приводят к получению аморфных немагнитных сплавов того же состава. После обработки при 500–600°С как аморфные, так и кристаллические сплавы переходили в более равновесную бинарную систему, содержащую твердый раствор W в Fe и интерметаллическое соединение. Концентрация оставшегося вольфрама в твердом растворе была много выше равновесной растворимости. В осадки включалось значительное количество водорода. Фактически полученные осадки могут быть квалифицированы как тройные сплавы Fe-W-H. Включенный водород играет решающую роль в переходе от кристаллического состояния, типичного для образцов, полученных при низкой плотности тока, к аморфным или нанокристаллическим осадкам, образованным при более высокой плотности тока</p></cfAbstr> <cfAbstr cfLangCode='EN' cfTrans='o'><p>Electrochemical deposition, structure, and properties of Fe-W alloys are studied, as well as their structure and properties. The alloys formed at a low current density are crystalline supersaturated solid solutions which are magnetic. At higher current densities, amorphous nonmagnetic alloys of the same composition are formed. As a result of treatment at 500–600°С, both amorphous and crystalline transform into a more equilibrium binary system, containing W solid solution in Fe and an intermetallic compound. The concentration of the remaining W in the solid solution was much higher than the equilibrium solubility. A considerable amount of hydrogen incorporates into the deposits. In fact, the deposits may be qualified as ternary Fe-W-H alloys. The incorporated hydrogen plays a crucial role in the transition from a crystalline state typical for specimens produced at low current densities to the amorphous or nanocrystalline deposits formed at higher current densities.. </p></cfAbstr> <cfResPubl_Class> <cfClassId>eda2d9e9-34c5-11e1-b86c-0800200c9a66</cfClassId> <cfClassSchemeId>759af938-34ae-11e1-b86c-0800200c9a66</cfClassSchemeId> <cfStartDate>2018-12-20T24:00:00</cfStartDate> </cfResPubl_Class> <cfResPubl_Class> <cfClassId>e601872f-4b7e-4d88-929f-7df027b226c9</cfClassId> <cfClassSchemeId>40e90e2f-446d-460a-98e5-5dce57550c48</cfClassSchemeId> <cfStartDate>2018-12-20T24:00:00</cfStartDate> </cfResPubl_Class> <cfPers_ResPubl> <cfPersId>ibn-person-15818</cfPersId> <cfClassId>49815870-1cfe-11e1-8bc2-0800200c9a66</cfClassId> <cfClassSchemeId>b7135ad0-1d00-11e1-8bc2-0800200c9a66</cfClassSchemeId> <cfStartDate>2018-12-20T24:00:00</cfStartDate> </cfPers_ResPubl> <cfPers_ResPubl> <cfPersId>ibn-person-60577</cfPersId> <cfClassId>49815870-1cfe-11e1-8bc2-0800200c9a66</cfClassId> <cfClassSchemeId>b7135ad0-1d00-11e1-8bc2-0800200c9a66</cfClassSchemeId> <cfStartDate>2018-12-20T24:00:00</cfStartDate> </cfPers_ResPubl> <cfFedId> <cfFedIdId>ibn-doi-69726</cfFedIdId> <cfFedId>10.5281/zenodo.1968647</cfFedId> <cfStartDate>2018-12-20T24:00:00</cfStartDate> <cfFedId_Class> <cfClassId>31d222b4-11e0-434b-b5ae-088119c51189</cfClassId> <cfClassSchemeId>bccb3266-689d-4740-a039-c96594b4d916</cfClassSchemeId> </cfFedId_Class> <cfFedId_Srv> <cfSrvId>5123451</cfSrvId> <cfClassId>eda2b2e2-34c5-11e1-b86c-0800200c9a66</cfClassId> <cfClassSchemeId>5a270628-f593-4ff4-a44a-95660c76e182</cfClassSchemeId> </cfFedId_Srv> </cfFedId> </cfResPubl> <cfPers> <cfPersId>ibn-Pers-15818</cfPersId> <cfPersName_Pers> <cfPersNameId>ibn-PersName-15818-1</cfPersNameId> <cfClassId>55f90543-d631-42eb-8d47-d8d9266cbb26</cfClassId> <cfClassSchemeId>7375609d-cfa6-45ce-a803-75de69abe21f</cfClassSchemeId> <cfStartDate>2018-12-20T24:00:00</cfStartDate> <cfFamilyNames>Гамбург </cfFamilyNames> <cfFirstNames>Ю.</cfFirstNames> </cfPersName_Pers> </cfPers> <cfPers> <cfPersId>ibn-Pers-60577</cfPersId> <cfPersName_Pers> <cfPersNameId>ibn-PersName-60577-1</cfPersNameId> <cfClassId>55f90543-d631-42eb-8d47-d8d9266cbb26</cfClassId> <cfClassSchemeId>7375609d-cfa6-45ce-a803-75de69abe21f</cfClassSchemeId> <cfStartDate>2018-12-20T24:00:00</cfStartDate> <cfFamilyNames>Захаров</cfFamilyNames> <cfFirstNames>Е.</cfFirstNames> </cfPersName_Pers> </cfPers> <cfSrv> <cfSrvId>5123451</cfSrvId> <cfName cfLangCode='en' cfTrans='o'>CrossRef DOI prefix service</cfName> <cfDescr cfLangCode='en' cfTrans='o'>The service of issuing DOI prefixes to publishers</cfDescr> <cfKeyw cfLangCode='en' cfTrans='o'>persistent identifier; Digital Object Identifier</cfKeyw> </cfSrv> </CERIF>
|
|
|