SM ISO690:2012 AYVAZYAN, G., KHUDAVERDYAN, Surik, MATEVOSYAN, Lenrik. Tunable Properties of Vacuum-Evaporated CH3NH3PbCl3-xIxx Perovskite Layers. In: IFMBE Proceedings: Nanotechnologies and Biomedical Engineering, Ed. 6, 20-23 septembrie 2023, Chişinău. Chişinău: Springer Science and Business Media Deutschland GmbH, 2023, Ediția 6, p. 52. ISBN 978-9975-72-773-0.. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
IFMBE Proceedings Ediția 6, 2023 |
||||||
Conferința "6th International Conference on Nanotechnologies and Biomedical Engineering" 6, Chişinău, Moldova, 20-23 septembrie 2023 | ||||||
|
||||||
Pag. 52-52 | ||||||
|
||||||
Descarcă PDF | ||||||
Rezumat | ||||||
Perovskite layers as a photo absorber material are widely used in single-junction and tandem solar cells. The characteristics of these solar cells have been greatly improved in recent years. This study prepared the CH3NH3PbI3−xClx metal halide perovskite layers on glass substrates covered with a thin indium tin oxide film by vacuum thermal evaporation method. Inorganic lead iodide (PbI2) and organic methylammonium chloride (CH3NH3Cl) were used as precursors. The layers were characterized by scanning electron microscope, x-ray diffraction, and C–V measurements. The transmission and absorption of the obtained layers were studied within the wavelength range of 400 to 1100 nm. It was found that the structural and optoelectronic properties of sequentially (layer-by-layer) evaporated (after annealing at the temperature of 100°C for 30 min) and co-evaporated (jointly) perovskite layers are similar. The perovskite layers had a tetragonal crystal structure. They densely, without pinholes and cracks covered the surface of the substrates. The layers show a favorable band gap of 1.57 eV. The low-temperature optical studies were carried out to reveal the temperature dependence of the band gap energy. The possibility of increasing the layers' thermal stability by adding 2.3 % cesium iodide to the PbI2 precursor during the evaporation process. was also shown. |
||||||
|