SM ISO690:2012 БОБАНОВА, Жанна, ПЕТРЕНКО, В., СИЛКИН, Сергей, ЮЩЕНКО, С., ЯХОВА, Е.. Электроосаждение аморфных сплавов Сo-W: роль гидродинамических условий. In: Электронная обработка материалов, 2005, nr. 6(41), pp. 86-91. ISSN 0013-5739. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Электронная обработка материалов | ||||||
Numărul 6(41) / 2005 / ISSN 0013-5739 /ISSNe 2345-1718 | ||||||
|
||||||
Pag. 86-91 | ||||||
|
||||||
Descarcă PDF | ||||||
Rezumat | ||||||
Results of study of amorphous Co-W alloys deposition from a citrate electrolyte in conditions of a stationary bath with fixed electrode and in controllable hydrodynamical conditions with application of rotating disk electrode (RDE) and RDE with excentricity are shown. It is demonstrated, that in stationary conditions W content in plated alloy grows with its thickness (from 5 up to 1011% at.). In conditions of intensive masstransfer W content in an alloy falls to 2.6% at. and does not depend on rotation speed. Increase of electrolyte рН up to 7 leads to growth of W content in alloy and its value becomes nearer to W content in alloy plated from stationary bath. It is supposed, that the determining factors influencing alloy composition are the рН value in the bulk electrolyte and masstransfer rate of electrode reactions products. These factors allow to control composition and morphology of received plating. |
||||||
|