 SM ISO690:2012TSYNTSARU, Natalia. Removal of barrier oxide in the anodized aluminum oxide nanotemplates. In: IFMBE Proceedings: 3rd International Conference on Nanotechnologies and Biomedical Engineering, ICNBME 2015, Ed. 3, 23-26 septembrie 2015, Chişinău. Springer, 2016, Editia 3, Vol.55, pp. 123-126. ISBN 978-981287735-2. ISSN 16800737. DOI: https://doi.org/10.1007/978-981-287-736-9_29 |
| EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
 IFMBE Proceedings Editia 3, Vol.55, 2016 |
||||||
|
Conferința "International Conference on Nanotechnologies and Biomedical Engineering" 3, Chişinău, Moldova, 23-26 septembrie 2015 | ||||||
|
||||||
| DOI:https://doi.org/10.1007/978-981-287-736-9_29 | ||||||
| Pag. 123-126 | ||||||
|
||||||
| Rezumat | ||||||
Aluminum as other valve metals possesses an important feature: it can form on the surface a porous structure – aluminium anodized oxide (AAO), under proper anodization conditions (voltage, pH, temperature, and etc). In order to be used as a template obtained AAO should undertake the barrier oxide removing step, which will ensure the appropriate electrical contact for material deposition. Thus, in this study we show the simple and unique method for barrier oxide thinning/removing by anodizing solution itself, in comparison with conventional procedure used. The more precise control of barrier oxide removing/ thinning was achieved in the same solution used as for anodisation, but at the temperature of 50 °C. |
||||||
| Cuvinte-cheie Aluminium anodized oxide, Anodic solution treatment, Barrier oxide layer, Zincate treatment |
||||||
|
|
|
|