SM ISO690:2012 BOTNARIUC, Vasile, GORCEAC, Leonid, KOVAL, Andrei, KETRUSH, Petru, CINIC, Boris, RAEVSKY, Simion, MICLI, Valdec. CdS nanometric layers grown on SnO2 coated glass substrates for photovoltaic devices. In: Fizică şi tehnică: procese, modele, experimente, 2012, nr. 1, pp. 11-15. ISSN 1857-0437. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Fizică şi tehnică: procese, modele, experimente | ||||||
Numărul 1 / 2012 / ISSN 1857-0437 | ||||||
|
||||||
CZU: 538.956 | ||||||
Pag. 11-15 | ||||||
|
||||||
Descarcă PDF | ||||||
Rezumat | ||||||
CdS layer thickness decreases at high substrate temperatures due to the fact that a part of CdCl2/(NH2)2 CS aqueous solution evaporates without reaching the substrate surface. CdS layers deposited at the substrate temperature from 250oC to 450oC are growing with a deficit of sulfur. CdS layers with better stoichiometry were grown in the conditions when in the solutions, used for CdS layers growing, there is an excess of thiourea (CdCl2/ TU =1:2). The high charge carrier concentration of 1020cm-3 in CdS layers grown on glass substrates coated with SnO2 layer is related to Sn doping of the layers from SnO2 layer. |
||||||
|
Cerif XML Export
<?xml version='1.0' encoding='utf-8'?> <CERIF xmlns='urn:xmlns:org:eurocris:cerif-1.5-1' xsi:schemaLocation='urn:xmlns:org:eurocris:cerif-1.5-1 http://www.eurocris.org/Uploads/Web%20pages/CERIF-1.5/CERIF_1.5_1.xsd' xmlns:xsi='http://www.w3.org/2001/XMLSchema-instance' release='1.5' date='2012-10-07' sourceDatabase='Output Profile'> <cfResPubl> <cfResPublId>ibn-ResPubl-33634</cfResPublId> <cfResPublDate>2012-01-03</cfResPublDate> <cfIssue>1</cfIssue> <cfStartPage>11</cfStartPage> <cfISSN>1857-0437</cfISSN> <cfURI>https://ibn.idsi.md/ro/vizualizare_articol/33634</cfURI> <cfTitle cfLangCode='EN' cfTrans='o'>CdS nanometric layers grown on SnO2 coated glass substrates for photovoltaic devices</cfTitle> <cfAbstr cfLangCode='EN' cfTrans='o'>CdS layer thickness decreases at high substrate temperatures due to the fact that a part of CdCl2/(NH2)2 CS aqueous solution evaporates without reaching the substrate surface. CdS layers deposited at the substrate temperature from 250oC to 450oC are growing with a deficit of sulfur. CdS layers with better stoichiometry were grown in the conditions when in the solutions, used for CdS layers growing, there is an excess of thiourea (CdCl2/ TU =1:2). The high charge carrier concentration of 1020cm-3 in CdS layers grown on glass substrates coated with SnO2 layer is related to Sn doping of the layers from SnO2 layer.</cfAbstr> <cfAbstr cfLangCode='RO' cfTrans='o'>Grosimea stratului de CdS se diminuiază la temperaturi ridicate ale substratului, datorită faptului că o parte din soluţia apoasă CdCl2/(NH2)2CS se evaporă fără a atinge suprafaţa substratului. Straturile CdS depuse la temperatura substratului de la 250°C la 450°C sînt în creştere cu un deficit de sulf. Straturi CdS cu o stoichiometrie mai bună au fost obţinute în condiţiile în care în soluţiile, utilizate pentru depunerea straturilor CdS, există exces de tiouree (CdCl2/ TU = 1:2). Concentraţia înaltă de transport de 1020 cm-3 în straturile CdS depuse pe substraturi de sticlă, acoperite cu un strat de SnO2, este legată de dopajul straturilor cu Sn din stratul SnO2.</cfAbstr> <cfResPubl_Class> <cfClassId>eda2d9e9-34c5-11e1-b86c-0800200c9a66</cfClassId> <cfClassSchemeId>759af938-34ae-11e1-b86c-0800200c9a66</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> </cfResPubl_Class> <cfResPubl_Class> <cfClassId>e601872f-4b7e-4d88-929f-7df027b226c9</cfClassId> <cfClassSchemeId>40e90e2f-446d-460a-98e5-5dce57550c48</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> </cfResPubl_Class> <cfPers_ResPubl> <cfPersId>ibn-person-42094</cfPersId> <cfClassId>49815870-1cfe-11e1-8bc2-0800200c9a66</cfClassId> <cfClassSchemeId>b7135ad0-1d00-11e1-8bc2-0800200c9a66</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> </cfPers_ResPubl> <cfPers_ResPubl> <cfPersId>ibn-person-1024</cfPersId> <cfClassId>49815870-1cfe-11e1-8bc2-0800200c9a66</cfClassId> <cfClassSchemeId>b7135ad0-1d00-11e1-8bc2-0800200c9a66</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> </cfPers_ResPubl> <cfPers_ResPubl> <cfPersId>ibn-person-1117</cfPersId> <cfClassId>49815870-1cfe-11e1-8bc2-0800200c9a66</cfClassId> <cfClassSchemeId>b7135ad0-1d00-11e1-8bc2-0800200c9a66</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> </cfPers_ResPubl> <cfPers_ResPubl> <cfPersId>ibn-person-23642</cfPersId> <cfClassId>49815870-1cfe-11e1-8bc2-0800200c9a66</cfClassId> <cfClassSchemeId>b7135ad0-1d00-11e1-8bc2-0800200c9a66</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> </cfPers_ResPubl> <cfPers_ResPubl> <cfPersId>ibn-person-45230</cfPersId> <cfClassId>49815870-1cfe-11e1-8bc2-0800200c9a66</cfClassId> <cfClassSchemeId>b7135ad0-1d00-11e1-8bc2-0800200c9a66</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> </cfPers_ResPubl> <cfPers_ResPubl> <cfPersId>ibn-person-1472</cfPersId> <cfClassId>49815870-1cfe-11e1-8bc2-0800200c9a66</cfClassId> <cfClassSchemeId>b7135ad0-1d00-11e1-8bc2-0800200c9a66</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> </cfPers_ResPubl> <cfPers_ResPubl> <cfPersId>ibn-person-46561</cfPersId> <cfClassId>49815870-1cfe-11e1-8bc2-0800200c9a66</cfClassId> <cfClassSchemeId>b7135ad0-1d00-11e1-8bc2-0800200c9a66</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> </cfPers_ResPubl> </cfResPubl> <cfPers> <cfPersId>ibn-Pers-42094</cfPersId> <cfPersName_Pers> <cfPersNameId>ibn-PersName-42094-3</cfPersNameId> <cfClassId>55f90543-d631-42eb-8d47-d8d9266cbb26</cfClassId> <cfClassSchemeId>7375609d-cfa6-45ce-a803-75de69abe21f</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> <cfFamilyNames>Botnariuc</cfFamilyNames> <cfFirstNames>Vasile</cfFirstNames> </cfPersName_Pers> </cfPers> <cfPers> <cfPersId>ibn-Pers-1024</cfPersId> <cfPersName_Pers> <cfPersNameId>ibn-PersName-1024-3</cfPersNameId> <cfClassId>55f90543-d631-42eb-8d47-d8d9266cbb26</cfClassId> <cfClassSchemeId>7375609d-cfa6-45ce-a803-75de69abe21f</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> <cfFamilyNames>Горчак</cfFamilyNames> <cfFirstNames>Л.</cfFirstNames> </cfPersName_Pers> </cfPers> <cfPers> <cfPersId>ibn-Pers-1117</cfPersId> <cfPersName_Pers> <cfPersNameId>ibn-PersName-1117-3</cfPersNameId> <cfClassId>55f90543-d631-42eb-8d47-d8d9266cbb26</cfClassId> <cfClassSchemeId>7375609d-cfa6-45ce-a803-75de69abe21f</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> <cfFamilyNames>Koval</cfFamilyNames> <cfFirstNames>Andrei</cfFirstNames> <cfFamilyNames>Коваль</cfFamilyNames> <cfFirstNames>Андрей</cfFirstNames> </cfPersName_Pers> </cfPers> <cfPers> <cfPersId>ibn-Pers-23642</cfPersId> <cfPersName_Pers> <cfPersNameId>ibn-PersName-23642-3</cfPersNameId> <cfClassId>55f90543-d631-42eb-8d47-d8d9266cbb26</cfClassId> <cfClassSchemeId>7375609d-cfa6-45ce-a803-75de69abe21f</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> <cfFamilyNames>Ketrush</cfFamilyNames> <cfFirstNames>Petru</cfFirstNames> </cfPersName_Pers> </cfPers> <cfPers> <cfPersId>ibn-Pers-45230</cfPersId> <cfPersName_Pers> <cfPersNameId>ibn-PersName-45230-3</cfPersNameId> <cfClassId>55f90543-d631-42eb-8d47-d8d9266cbb26</cfClassId> <cfClassSchemeId>7375609d-cfa6-45ce-a803-75de69abe21f</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> <cfFamilyNames>Cinic</cfFamilyNames> <cfFirstNames>Boris</cfFirstNames> </cfPersName_Pers> </cfPers> <cfPers> <cfPersId>ibn-Pers-1472</cfPersId> <cfPersName_Pers> <cfPersNameId>ibn-PersName-1472-3</cfPersNameId> <cfClassId>55f90543-d631-42eb-8d47-d8d9266cbb26</cfClassId> <cfClassSchemeId>7375609d-cfa6-45ce-a803-75de69abe21f</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> <cfFamilyNames>Raevsky</cfFamilyNames> <cfFirstNames>Simion</cfFirstNames> <cfFamilyNames>Раевский</cfFamilyNames> <cfFirstNames>С.</cfFirstNames> </cfPersName_Pers> </cfPers> <cfPers> <cfPersId>ibn-Pers-46561</cfPersId> <cfPersName_Pers> <cfPersNameId>ibn-PersName-46561-3</cfPersNameId> <cfClassId>55f90543-d631-42eb-8d47-d8d9266cbb26</cfClassId> <cfClassSchemeId>7375609d-cfa6-45ce-a803-75de69abe21f</cfClassSchemeId> <cfStartDate>2012-01-03T24:00:00</cfStartDate> <cfFamilyNames>Micli</cfFamilyNames> <cfFirstNames>Valdec</cfFirstNames> </cfPersName_Pers> </cfPers> </CERIF>