![]() PARASCHIV, Dragoş, POPA, Sergiu, HERGHEA, D., ENCULESCU, Eu., MARIN, Adriana. Nanodepuneri dure PVD, pe baza de titan. Prezent si perspective. In: Inginerie agrară şi transport auto, 12-13 noiembrie 2015, Chișinău. Chișinău, Republica Moldova: Universitatea Agrară de Stat din Moldova, 2015, Vol.45, pp. 179-187. ISBN 978-9975-64-276-7. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Inginerie agrară şi transport auto Vol.45, 2015 |
||||||
Simpozionul "Realizări şi perspective în inginerie agrară şi transport auto" Chișinău, Moldova, 12-13 noiembrie 2015 | ||||||
|
||||||
CZU: 669 | ||||||
Pag. 179-187 | ||||||
|
||||||
![]() |
||||||
Rezumat | ||||||
In this paper we will elaborate a statistic analysis on the main parameters which influence the tribologic depositions process of thin TiN and anather layers. The deposition of tribologic layers will be executed on the axes of the supercharging turbines at the automobiles made of C120, the maximum allowed thickness being of 1÷1.5μm. The main stages of the TiN coating operation are washing and drying conditions which we relate to adhesion layer deposited titanium and titanium coating process, the process consists of important elements of the TiN coating (Electron heating time-Argon plasma, electron temperature, plasma heating argon for Bias voltage ramp., Bias voltage temperature ramp., temperature ion cleaning time for coating titanium pressure nitrogen nitrogen temperature) relative to the thickness of the deposited titanium. The operation of coating with a layer of TiN will be done on a DREVA 400 machine at S.C. “Rulmenti” S.A. Barlad. After determining the parameters and the following measurements determining these parameters for deposition of hard coatings axis turbines will be testing them in an accelerated regimen own conception stand. Statistical analysis parameters and accelerated testing will be done with MiniTab 14 software. |
||||||
Cuvinte-cheie tribologic layers, thin TiN, TiAlN, AlCrN layers, physical method |
||||||
|