The optical transmission spectrums for ZnSe thin films have been obtained in the spectral domain of 330 – 1400 nm. With the growth of the film thickness we observe a growth in the number of interference maxims and minims, and for the thickness of d > 0.77μm, the difference between maximal and minimal transmission decreases. The presence of interference maxims and minims in transmission spectrums is determined by the multiple reflections from the film surface and represents an index that the samples are uniform and that film surfaces are plane. For thin layers with thickness d < 0.60 μm heat treatment leads to an increase in maximum and minimum interference, while for phase with the thickness d > 0.60 μm thermal treatment practically does not change the shape of the transmission spectrum.

Spectrele de transmisie optică pentru straturile subţiri de ZnSe au fost obţinute în domeniul spectral 330-1400nm. Odată cu creşterea grosimii straturilor, creşte şi numărul maximelor şi minimelor de interferenţă, iar pentru grosimi d > 0.77μm diferenţa dintre transmisia maximă şi minimă se micşorează. Prezenţa maximelor şi minimelor de interferenţă în spectrele de transmisie sunt datorate reflexiilor multiple de pe suprafaţa stratului şi reprezintă un indiciu că probele sunt uniforme şi că suprafeţele straturilor sunt plane. Pentru straturile subţiri cu grosimi d < 0.60μm tratamentul termic conduce la creşterea numărului de maxime şi minime de interferenţă, iar pentru cele cu grosimi d > 0.60μm tratamentul termic, practic, nu modifică forma spectrului de transmisie.