SM ISO690:2012 MORARI, Vadim, RUSU, Emil, URSAKI, Veaceslav, NIELSCH, Kornelius, TIGINYANU, Ion. Aerosol Spray Deposited Wurtzite ZnMgO Alloy Films with MgO Nanocrystalline Inclusions. In: Nanotechnologies and Biomedical Engineering, Ed. 5, 3-5 noiembrie 2021, Chişinău. Chişinău: Pontos, 2021, Ediția 5, p. 62. ISBN 978-9975-72-592-7. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Nanotechnologies and Biomedical Engineering Ediția 5, 2021 |
||||||
Conferința "Nanotechnologies and Biomedical Engineering" 5, Chişinău, Moldova, 3-5 noiembrie 2021 | ||||||
|
||||||
Pag. 62-62 | ||||||
|
||||||
Descarcă PDF | ||||||
Rezumat | ||||||
In this paper Zn1-xMgxO thin films with composition range x = 0.00 – 0.80 have been obtained by aerosol spray deposition method on p-Si substrates by using zinc acetate and magnesium acetate as precursors. The produced thin films were characterized by scanning electron microscopy (SEM), energy dispersive X-ray (EDX) analysis, X-ray diffraction (XRD), and optical spectroscopy. SEM images revealed uniform nanocrystalline morphology of films, but the form of nanocrystals vary with variation of the Mg content. XRD analysis suggests that the produced films contain a wurtzite Zn1-xMgxO phase in the whole chemical composition range, with cubic phase MgO nanocrystalline inclusions with mean grain size around 20 nm. The optical bandgap was found to vary from 3.4 eV to 5.2 eV with increasing the Mg content from 0 to 60%. |
||||||
|