![]() BUNEA, Marina. Studiul rezistenței la oboseală a compozitelor termorigide armate cu fibre. In: Inovaţia: factor al dezvoltării social-economice, 22 decembrie 2017, Cahul. Cahul, Republica Moldova: Universitatea de Stat „Bogdan Petriceicu Hasdeu” din C, 2017, pp. 147-151. ISBN 978-9975-88-025-1. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Inovaţia: factor al dezvoltării social-economice 2017 | ||||||
Conferința "Inovaţia: factor al dezvoltării social-economice" Cahul, Moldova, 22 decembrie 2017 | ||||||
|
||||||
Pag. 147-151 | ||||||
|
||||||
![]() |
||||||
Rezumat | ||||||
In this review the issues of fatigue strength of fiber reinforced thermoset composites are presented. The effects of the fiber types, fiber-matrix interface quality, fiber volume fraction, fabric weave types and fiber orientation on the fracture resistance are discussed. |
||||||
Cuvinte-cheie composites, fatigue response, cyclic strains, peak stress, Failure mode |
||||||
|
DataCite XML Export
<?xml version='1.0' encoding='utf-8'?> <resource xmlns:xsi='http://www.w3.org/2001/XMLSchema-instance' xmlns='http://datacite.org/schema/kernel-3' xsi:schemaLocation='http://datacite.org/schema/kernel-3 http://schema.datacite.org/meta/kernel-3/metadata.xsd'> <creators> <creator> <creatorName>Bunea, M.</creatorName> <affiliation>Universitatea de Stat „Bogdan Petriceicu Hasdeu“, Cahul, Moldova, Republica</affiliation> </creator> </creators> <titles> <title xml:lang='ro'>Studiul rezistenței la oboseală a compozitelor termorigide armate cu fibre</title> </titles> <publisher>Instrumentul Bibliometric National</publisher> <publicationYear>2017</publicationYear> <relatedIdentifier relatedIdentifierType='ISBN' relationType='IsPartOf'>978-9975-88-026-8</relatedIdentifier> <subjects> <subject>composites</subject> <subject>fatigue response</subject> <subject>cyclic strains</subject> <subject>peak stress</subject> <subject>Failure mode</subject> </subjects> <dates> <date dateType='Issued'>2017</date> </dates> <resourceType resourceTypeGeneral='Text'>Conference Paper</resourceType> <descriptions> <description xml:lang='en' descriptionType='Abstract'><p>In this review the issues of fatigue strength of fiber reinforced thermoset composites are presented. The effects of the fiber types, fiber-matrix interface quality, fiber volume fraction, fabric weave types and fiber orientation on the fracture resistance are discussed.</p></description> </descriptions> <formats> <format>application/pdf</format> </formats> </resource>