SM ISO690:2012 БАХАДИРХАНОВ, М., ИБРАГИМОВ, Ш., КАМОЛОВ, И.. Влияние химической обработки на поверхностные состояния и электрофизические характеристики Au-n-InP структур. In: Электронная обработка материалов, 2004, nr. 2(40), pp. 92-95. ISSN 0013-5739. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Электронная обработка материалов | ||||||
Numărul 2(40) / 2004 / ISSN 0013-5739 /ISSNe 2345-1718 | ||||||
|
||||||
Pag. 92-95 | ||||||
|
||||||
Descarcă PDF | ||||||
Rezumat | ||||||
The paper reports the results of investigations of chemical processing influence on parameters of Schottky barriers M-InP. The influence was estimated according to CVD and VFD of contacts Аu-n-InP (100) (S = 4,10 - 2 cm2) formed by the method thermal deposition of Au on substrates n-InP (N = 1018 сm3), 403 - 423 K. It is shown, that chemical processing is the important factor of control of the superficial properties of InP which effect practically on all parameters of contacts Au-n-InP. At variation of a kind of chemical processing the factor of non-ideality of CVD, эф б Ф and the voltage of breakdown can change within the limits of 1,06 - 1,8, 0,35 - 0,68 eV and 3 -10 V, respectively. At the analysis of electric characteristics of contacts Au-n-InP it is seen that Schottky barriers received on a surface that was processed in alkaline medium (рН > 7) possess weaker temperature dependence Is . This fact testifies about decreased Фб Т of such contacts. |
||||||
|
Google Scholar Export
<meta name="citation_title" content="Влияние химической обработки на поверхностные состояния и электрофизические характеристики Au-n-InP структур"> <meta name="citation_author" content="Бахадирханов М."> <meta name="citation_author" content="Ибрагимов Ш."> <meta name="citation_author" content="Камолов И."> <meta name="citation_publication_date" content="2004/05/01"> <meta name="citation_journal_title" content="Электронная обработка материалов"> <meta name="citation_volume" content="40"> <meta name="citation_issue" content="2"> <meta name="citation_firstpage" content="92"> <meta name="citation_lastpage" content="95"> <meta name="citation_pdf_url" content="https://ibn.idsi.md/sites/default/files/imag_file/92-95_35.pdf">