SM ISO690:2012 SARANŢEV, V., МАРКОВА, Л., АЗАРЕНКО, Е.. Исследование композиционных электроискровых
покрытий на основе карбида титана с использованием самораспространяющегося
высокотемпературного синтеза
. In: Электронная обработка материалов, 2012, nr. 2(48), pp. 43-49. ISSN 0013-5739. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Электронная обработка материалов | ||||||
Numărul 2(48) / 2012 / ISSN 0013-5739 /ISSNe 2345-1718 | ||||||
|
||||||
Pag. 43-49 | ||||||
|
||||||
Descarcă PDF | ||||||
Rezumat | ||||||
The composite coatings obtained by the method of electrospark doping and the self-propagating high-temperature synthesis have been examined. It is revealed that the generated composite coatings consist of the titanium carbides which are uniformly distributed in the metal matrix. The grains of titanium carbide are of the size of 0,1–4,0 microns. Large titanium carbide grains in the coatings consist of disperse carbides of the size less than 1 micron. The investigation of the structure of the composite coatings in the friction
tracks after the performed tests has shown that the formed coatings have high wearing capacity. |
||||||
|
Dublin Core Export
<?xml version='1.0' encoding='utf-8'?> <oai_dc:dc xmlns:dc='http://purl.org/dc/elements/1.1/' xmlns:oai_dc='http://www.openarchives.org/OAI/2.0/oai_dc/' xmlns:xsi='http://www.w3.org/2001/XMLSchema-instance' xsi:schemaLocation='http://www.openarchives.org/OAI/2.0/oai_dc/ http://www.openarchives.org/OAI/2.0/oai_dc.xsd'> <dc:creator>Saranţev, V.V.</dc:creator> <dc:creator>Marcova, L.V.</dc:creator> <dc:creator>Azarenco, E.L.</dc:creator> <dc:date>2012-03-01</dc:date> <dc:description xml:lang='en'>The composite coatings obtained by the method of electrospark doping and the self-propagating high-temperature synthesis have been examined. It is revealed that the generated composite coatings consist of the titanium carbides which are uniformly distributed in the metal matrix. The grains of titanium carbide are of the size of 0,1–4,0 microns. Large titanium carbide grains in the coatings consist of disperse carbides of the size less than 1 micron. The investigation of the structure of the composite coatings in the friction tracks after the performed tests has shown that the formed coatings have high wearing capacity.</dc:description> <dc:description xml:lang='ru'>Исследованы композиционные покрытия, полученные методом электроискрового легирования и самораспространяющегося высокотемпературного синтеза. Установлено, что сформированные композиционные покрытия состоят из карбидов титана, равномерно распределенных в металлической матрице. Величина зерен карбида титана – 0,1–4,0 мкм. Крупные зерна карбида титана в покрытии состоят из дисперсных карбидов с размерами менее 1 мкм. Исследование структуры композиционных покрытий в дорожках трения после проведенных испытаний показало, что формируемые покрытия имеют высокую износостойкость.</dc:description> <dc:source>Электронная обработка материалов (2(48)) 43-49</dc:source> <dc:title>Исследование композиционных электроискровых покрытий на основе карбида титана с использованием самораспространяющегося высокотемпературного синтеза </dc:title> <dc:type>info:eu-repo/semantics/article</dc:type> </oai_dc:dc>