In this study, the electroless method was successfully used to deposit composite coatings containing B4C nanoparticles on Ck45 carbon steel. The characteristics of coatings were investigated with the X-ray diffraction (XRD) and scanning electron microscopy (SEM). The hardness of coatings was measured by Vickers micro-hardness test with a load of 1 N. The hardness of the composite coating of Ni-B-B4C was about 870 Vickers, which increased to 1350 Vickers after heat treatment at 400C for 1 hour, which was much more than for Ni-B coating and Ck45 steel. The wear test was carried out using the pin-on-disk test technique. The results indicated an improvement in the wear resistance of Ni-B-B4C composite coatings compared to that of Ni-B and Ck45. The results obtained from the Tafel polarization test indicated an increase in the corrosion resistance of Ni-B-B4C composite coatings compared to that of Ni-B coatings and Ck45 steel.

В настоящем исследовании успешно был использован метод химического осаждения для получения композитных покрытий с включением наночастиц B4C на углеродистой стали Ck45. Характеристики покрытий исследовали методами энергодисперсионной спектрометрии и сканирующей электронной микроскопии. Твердость покрытия измерялась с применением микротвердомра Викерса под нагрузкой 1Н. Твердость композитного покрытия Ni-B-B4C HV ~ 870 после термообработки при 400C в течение 1 часа увеличивалась до HV = 1350, что гораздо больше, чем твердость покрытий никель-бор и стали Ck45. При испытаниях на износ использовалась методика штифт-диск. Результаты показали улучшение износостойкости композитных покрытий Ni-B-B4C по сравнению с покрытиями никель-бор и сталью Ck45. Результаты, полученные при использовании метода таффелевской поляризации, показали увеличение коррозионной стойкости по сравнению с покрытиями никель-бор и сталью Ck45.