The corrosion of copper – nickel alloy in hydrochloric acid has been investigated at different temperatures, benzotrizole concentrations and corrosive solution velocities. Weight loss technique has been used to evaluate the corrosion rate data. Results obtained have proved that benzotrizole has a dual effect by reducing both metal corrosion and flow losses. Maximum inhibition efficiency was 91.5%, while maximum drag reduction was 52.4%. Several mathematical equations are suggested successfully to represent the data with high correlation coefficients. Molecular dynamic simulations have been also performed to investigate the adsorption behavior of the inhibitor on the copper alloy surface. One of the novelties of the given work is the analogy between the corrosion process and fluid flow, as well as the investigation of the dual effect of benzotriazole on the corrosion process and the flow losses.

Объектом исследования была коррозия медно- никелевого сплава, погруженного в соляную кислоту, при разных температурах, концентрациях бензотриазола и скоростях коррозии. Для оценки скорости коррозии использовался метод определения потерь в массе. Полученные результаты показали двойной эффект применения бензотриазола: уменьшилась как коррозия сплава, так и потери в потоке соляной кислоты. Максимальная эффективность ингибирования составила 91,5%, а максимальное уменьшение наволакива ния меди было равно 52,4%. Предложен ряд уравнений, описывающих полученные экспериментальные данные с высоким коэффициентом соответствия. Динамическое молекулярное моделирование было применено при исследовании режима адсорбции ингибитора на поверхности медного сплава. Новым в данной работе является проведение аналогии между процессом коррозии и поведением потока соляной кислоты, а также исследование двойного эффекта применения бензотриазола: как ингибитора коррозии и добавки, способствующей уменьшению потерь соляной кислоты.