Nano and Microparticles of Iron with a Modified Surface and Prospects for Their Application. Part I: Copper Coated Iron Particles
Закрыть
Conţinutul numărului revistei
Articolul precedent
Articolul urmator
789 0
SM ISO690:2012
VARYUKHIN, V., KHIZHENKOV, P., MAKMAK, I., SIROTKIN, V., PANCHENKO, L.. Nano and Microparticles of Iron with a Modified Surface and Prospects for Their Application. Part I: Copper Coated Iron Particles. In: Surface Engineering and Applied Electrochemistry, 2011, nr. 5(47), pp. 399-402. ISSN 1068-3755.
EXPORT metadate:
Google Scholar
Crossref
CERIF

DataCite
Dublin Core
Surface Engineering and Applied Electrochemistry
Numărul 5(47) / 2011 / ISSN 1068-3755 /ISSNe 1934-8002

Nano and Microparticles of Iron with a Modified Surface and Prospects for Their Application. Part I: Copper Coated Iron Particles

Pag. 399-402

Varyukhin V., Khizhenkov P., Makmak I., Sirotkin V., Panchenko L.
 
 
Disponibil în IBN: 29 noiembrie 2013


Rezumat

The catalytic properties of metal copper in chemical reactions between ferrite garnet materials and orthophosphoric acid are described. It was shown that the reactions occur more efficiently provided copper is used in the form of shells on nano and microparticles of iron and stirring of the etching agent is performed by the magnetic fields. The formation of the metal copper on iron particles is carried out using a chemical method owing to the reaction between the iron particles and the water solution of blue vitriol and sulphuric acid. The highest efficiency of stirring is registered using a magnetic field with a variable direction of the magnetic field gradient.