Micro-Raman spectra of bulk GexAsxSe1-2X chalcogenide glasses
Закрыть
Conţinutul numărului revistei
Articolul precedent
Articolul urmator
711 0
SM ISO690:2012
IASENIUC, Oxana, YOVU, M., GHIULNARE, A., MESTERCA, Raluca, JDERU, A., ENACHESCU, Marius. Micro-Raman spectra of bulk GexAsxSe1-2X chalcogenide glasses. In: Proceedings of the Romanian Academy Series A - Mathematics Physics Technical Sciences Information Science, 2018, vol. 19, pp. 545-550. ISSN 1454-9069.
EXPORT metadate:
Google Scholar
Crossref
CERIF

DataCite
Dublin Core
Proceedings of the Romanian Academy Series A - Mathematics Physics Technical Sciences Information Science
Volumul 19 / 2018 / ISSN 1454-9069

Micro-Raman spectra of bulk GexAsxSe1-2X chalcogenide glasses


Pag. 545-550

Iaseniuc Oxana1, Yovu M.1, Ghiulnare A.2, Mesterca Raluca2, Jderu A.2, Enachescu Marius23
 
1 Institute of Applied Physics,
2 University Politehnica of Bucharest,
3 Romanian Academy of Science
 
Disponibil în IBN: 21 iunie 2019


Rezumat

In this work are reported the Micro-Raman spectra of GexAsxSe1-2x (x = 0.05÷0.30). The Micro-Raman spectra consist of three main peaks located around ν = 193 cm-1, ν = 213 cm-1, and ν = 255 cm-1. The peaks around ν = 193 cm-1 and ν = 213 cm-1 could be attributed to the vibration of GeSe bonds. The presence of the Raman peak at ν = 255 cm-1 is due to the bond-stretching vibration of the disordered Se chains and rings. With the increase of the Ge concentration this peak shifts to a higher wavenumber due to the shortening of Se chains. The peak around ν = 300 cm-1 is characteristic to Ge-Ge vibration mode. The Ge concentration slightly changes the shape of Micro-Raman spectra, mainly its ratio of the intensity.

Cuvinte-cheie
chalcogenide glasses, Coordination number, Micro-, Raman spectra