Detectors based on Pd-doped and PdO-functionalized ZnO nanostructures
Закрыть
Articolul precedent
Articolul urmator
411 2
Ultima descărcare din IBN:
2023-05-08 17:42
SM ISO690:2012
POSTICA, Vasile, LUPAN, Oleg, ABABII, Nicolai, HOPPE, Mathias, ADELUNG, Rainer, CHOW, Lee, SHONTYA, Viktor, ASCHEHOUG, Patrick, VIANA, Bruno, PAUPORTE, Thierry. Detectors based on Pd-doped and PdO-functionalized ZnO nanostructures. In: Proceedings of SPIE - The International Society for Optical Engineering, Ed. 9, 28 ianuarie - 1 februarie 2018, San Francisco. Bellingham, Washington USA: SPIE, 2018, Ediția 9, Vol.10533, pp. 1-7. ISBN 978-151061551-9. ISSN 0277786X. DOI: https://doi.org/10.1117/12.2294945
EXPORT metadate:
Google Scholar
Crossref
CERIF

DataCite
Dublin Core
Proceedings of SPIE - The International Society for Optical Engineering
Ediția 9, Vol.10533, 2018
Conferința "Oxide-Based Materials and Devices "
9, San Francisco, Statele Unite ale Americii, 28 ianuarie - 1 februarie 2018

Detectors based on Pd-doped and PdO-functionalized ZnO nanostructures

DOI: https://doi.org/10.1117/12.2294945

Pag. 1-7

Postica Vasile1, Lupan Oleg123, Ababii Nicolai1, Hoppe Mathias3, Adelung Rainer3, Chow Lee4, Shontya Viktor1, Aschehoug Patrick2, Viana Bruno2, Pauporte Thierry2
 
1 Technical University of Moldova,
2 PSL Research University, Chimie ParisTech - CNRS, Institut de Recherche de Chimie Paris,
3 Institute for Material Science, Christian-Albrechts-University of Kiel,
4 University of Central Florida
 
Disponibil în IBN: 10 iunie 2021


Rezumat

In this work, zinc oxide (ZnO) nanostructured films were grown using a simple synthesis from chemical solutions (SCS) approach from aqueous baths at relatively low temperatures (< 95°C). The samples were doped with Pd (0.17 at% Pd) and functionalized with PdO nanoparticles (NPs) using the PdCl2 aqueous solution and subsequent thermal annealing at 650°C for 30 min. The morphological, micro-Raman and optical properties of Pd modified samples were investigated in detail and were demonstrated to have high crystallinity. Gas sensing studies unveiled that compared to pure ZnO films, the Pd-doped ZnO (ZnO:Pd) nanostructured films showed a decrease in ethanol vapor response and slight increase in H2 response with low selectivity. However, the PdO-functionalized samples showed excellent H2 gas sensing properties with possibility to detect H2 gas even at room temperature (gas response of ∼ 2). Up to 200°C operating temperature the samples are highly selective to H2 gas, with highest response of ∼ 12 at 150°C. This study demonstrates that surface functionalization of n-ZnO nanostructured films with p-type oxides is very important for improvement of gas sensing properties. 