| Conţinutul numărului revistei |
| Articolul precedent |
| Articolul urmator |
 |
 915 4 |
| Ultima descărcare din IBN: 2023-02-15 18:58 |
 SM ISO690:2012TSYNTSARU, Natalia, VOLODINA, Galina, BERSIROVA, Oksana, DIKUSAR, Aleksandr , BELEVSKII, Stanislav, IAPONTSEVA, Iu., KUBLANOVSKY, Valeriy. Composition, Structure, and Corrosion Properties of Coatings of Co–W Alloys Electrodeposited under Direct Current. In: Surface Engineering and Applied Electrochemistry, 2007, nr. 5(43), pp. 312-317. ISSN 1068-3755. |
| EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
| Surface Engineering and Applied Electrochemistry | ||||||
| Numărul 5(43) / 2007 / ISSN 1068-3755 /ISSNe 1934-8002 | ||||||
|
||||||
| Pag. 312-317 | ||||||
|
||||||
 Descarcă PDF |
||||||
| Rezumat | ||||||
A correlation has been found between the composition, structure, and corrosion resistance of electrolytic Co–W coatings (on the basis of voltammeter and impedance measurements at pH-6.0 in a chloride–sulfate model solution) deposited at various densities of direct current from citrate electrolyte with a high concentration of sodium tungstate with addition of boric acid at a temperature of 58°C. It is found that these coat-
ings possess a high corrosion resistance that is only insignificantly inferior to that of electrolyte chromium coatings. We have determined the interval of current densities of electrodeposition in which corrosion resistance of the coatings is maximum.
|
||||||
|
|
|
|