Synthesis and Characterization of Hydroxy-Chromium Pillared Bentonite
Închide
Conţinutul numărului revistei
Articolul precedent
Articolul urmator
849 1
Ultima descărcare din IBN:
2023-05-08 10:02
SM ISO690:2012
ARFAOUI, S., FRINI-SRASRA, N., SRASRA, Ezzedine. Synthesis and Characterization of Hydroxy-Chromium Pillared Bentonite . In: Surface Engineering and Applied Electrochemistry, 2009, nr. 3(45), pp. 239-245. ISSN 1068-3755.
EXPORT metadate:
Google Scholar
Crossref
CERIF

DataCite
Dublin Core
Surface Engineering and Applied Electrochemistry
Numărul 3(45) / 2009 / ISSN 1068-3755 /ISSNe 1934-8002

Synthesis and Characterization of Hydroxy-Chromium Pillared Bentonite

Pag. 239-245

Arfaoui S., Frini-Srasra N., Srasra Ezzedine
 
 
Disponibil în IBN: 30 noiembrie 2013


Rezumat

Chromium pillared clays, in particular, have attracted the researchers attention after being tested as catalyst in a wide range of reactions, like catalytic conversion of hydrocarbons, ester formation and elimination of water from alcohols. The chromium oligomers used for intercalation were prepared by addition of Na2CO3 to a chromium nitrate solution or chromium chlorite solution and the mixture is heated at 80°C for 36 h. The pillaring clay is obtained by heating intercalated bentonite at 360°C under vacuum. Several Techniques, X-ray diffraction, N2 adsorption–desorption isotherms and chemical analysis have been used to characterize and to compare the properties of the materials synthesized. Our study consists in determination of the influence of the intercalated OH–Cr group on the structure of Tunisian bentonite. The results showed that the interlamellar distances of pillared bentonite ranged from 17 to 21 Å. In addition, the synthesized clays exhibit increased BET surface areas and higher micro pore volumes compared with unmodified clay. On the other hand, the micro pore surface area, the micro pore volume and the d (001) spacing after pillaring increased with the amount of chromium retentions.