Design of highly active electrodes for hydrogen evolution reaction based on mo-rich alloys electrodeposited from ammonium acetate bath
Închide
Conţinutul numărului revistei
Articolul precedent
Articolul urmator
90 0
SM ISO690:2012
VERNICKAITE, E.; BERSIROVA, Oksana; CESIULIS, Henrikas; TSYNTSARU, Natalia. Design of highly active electrodes for hydrogen evolution reaction based on mo-rich alloys electrodeposited from ammonium acetate bath. In: Coatings. 2019, nr. 2(9), p. 0. ISSN 2079-6412.
10.3390/COATINGS9020085
EXPORT metadate:
Google Scholar
Crossref
CERIF
BibTeX
DataCite
Dublin Core
Coatings
Numărul 2(9) / 2019 / ISSN 2079-6412

Design of highly active electrodes for hydrogen evolution reaction based on mo-rich alloys electrodeposited from ammonium acetate bath


DOI: 10.3390/COATINGS9020085
Pag. 0-0

Vernickaite E.1, Bersirova Oksana2, Cesiulis Henrikas1, Tsyntsaru Natalia31
 
1 Vilnius University,
2 Vernadsky Institute of General and Inorganic Chemistry NAS Ukraine ,
3 Institute of Applied Physics
 
Disponibil în IBN: 7 octombrie 2019


Rezumat

The given research was driven by prospects to design Mo-rich coatings with iron group metals electrodeposited from a highly saturated ammonium acetate bath. The obtained coatings could be employed as prominent electrodes for the hydrogen evolution reaction (HER). It was found that the Mo content in Ni-Mo alloys can be tuned from 30 to 78 at.% by decreasing the molar ratio [Ni(II)]:[Mo(VI)] in the electrolyte from 1.0 to 0.25 and increasing the cathodic current density from 30 to 100 mA/cm2. However, dense cracks and pits are formed due to hydrogen evolution at high current densities and that diminishes the catalytic activity of the coating for HER. Accordingly, smoother and crack-free Ni-54 at.% Mo, Co-52 at.% Mo and Fe-54 at.% Mo alloys have been prepared at 30 mA/cm2. Their catalytic behavior for HER has been investigated in a 30 wt.% NaOH solution at temperatures ranging from 25 to 65 °C. A significant improvement of electrocatalytic activity with increasing bath temperature was noticed. The results showed that the sequence of electrocatalytic activity in alkaline media decreases in the following order: Co-52 at.% Mo > Ni-54 at.% Mo > Fe-54 at.% Mo. These peculiarities might be linked with different catalytic behavior of formed intermetallics (and active sites) in electrodeposited alloys. The designed electrodeposited Mo-rich alloys have a higher catalytic activity than Mo and Pt cast metals.

Cuvinte-cheie
Co-Mo, Electrocatalysis, Electrodeposition, Fe-Mo alloys, Hydrogen evolution reaction, Ni-Mo

Dublin Core Export

<?xml version='1.0' encoding='utf-8'?>
<oai_dc:dc xmlns:dc='http://purl.org/dc/elements/1.1/' xmlns:oai_dc='http://www.openarchives.org/OAI/2.0/oai_dc/' xmlns:xsi='http://www.w3.org/2001/XMLSchema-instance' xsi:schemaLocation='http://www.openarchives.org/OAI/2.0/oai_dc/ http://www.openarchives.org/OAI/2.0/oai_dc.xsd'>
<dc:creator>Angheluţa, V.F.</dc:creator>
<dc:date>2015</dc:date>
<dc:source>Tendinţe contemporane ale dezvoltării ştiinţei: viziuni ale tinerilor cercetători () 96-96</dc:source>
<dc:title><p>Cercetarea peisajului - domeniu actual &icirc;ntr-o lume &icirc;n schimbare</p></dc:title>
<dc:type>info:eu-repo/semantics/article</dc:type>
</oai_dc:dc>