 SM ISO690:2012IASENIUC, Oxana, YOVU, M., GHIULNARE, A., MESTERCA, Raluca, JDERU, A., ENACHESCU, Marius. Micro-Raman spectra of bulk GexAsxSe1-2X chalcogenide glasses. In: Proceedings of the Romanian Academy Series A - Mathematics Physics Technical Sciences Information Science, 2018, vol. 19, pp. 545-550. ISSN 1454-9069. |
| EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
  Proceedings of the Romanian Academy Series A - Mathematics Physics Technical Sciences Information Science |
||||||
| Volumul 19 / 2018 / ISSN 1454-9069 | ||||||
|
||||||
| Pag. 545-550 | ||||||
|
||||||
| Rezumat | ||||||
In this work are reported the Micro-Raman spectra of GexAsxSe1-2x (x = 0.05÷0.30). The Micro-Raman spectra consist of three main peaks located around ν = 193 cm-1, ν = 213 cm-1, and ν = 255 cm-1. The peaks around ν = 193 cm-1 and ν = 213 cm-1 could be attributed to the vibration of GeSe bonds. The presence of the Raman peak at ν = 255 cm-1 is due to the bond-stretching vibration of the disordered Se chains and rings. With the increase of the Ge concentration this peak shifts to a higher wavenumber due to the shortening of Se chains. The peak around ν = 300 cm-1 is characteristic to Ge-Ge vibration mode. The Ge concentration slightly changes the shape of Micro-Raman spectra, mainly its ratio of the intensity. |
||||||
| Cuvinte-cheie chalcogenide glasses, Coordination number, Micro-, Raman spectra |
||||||
|
Dublin Core Export
<?xml version='1.0' encoding='utf-8'?> <oai_dc:dc xmlns:dc='http://purl.org/dc/elements/1.1/' xmlns:oai_dc='http://www.openarchives.org/OAI/2.0/oai_dc/' xmlns:xsi='http://www.w3.org/2001/XMLSchema-instance' xsi:schemaLocation='http://www.openarchives.org/OAI/2.0/oai_dc/ http://www.openarchives.org/OAI/2.0/oai_dc.xsd'> <dc:creator>Iaseniuc, O.V.</dc:creator> <dc:creator>Iovu, M.S.</dc:creator> <dc:creator>Ghiulnare, A.</dc:creator> <dc:creator>Mesterca, R.</dc:creator> <dc:creator>Jderu, A.</dc:creator> <dc:creator>Enăchescu, M.</dc:creator> <dc:date>2018-12-01</dc:date> <dc:description xml:lang='en'><p>In this work are reported the Micro-Raman spectra of Ge<sub>x</sub>As<sub>x</sub>Se<sub>1-2x</sub> (x = 0.05÷0.30). The Micro-Raman spectra consist of three main peaks located around ν = 193 cm<sup>-1</sup>, ν = 213 cm<sup>-1</sup>, and ν = 255 cm<sup>-1</sup>. The peaks around ν = 193 cm<sup>-1</sup> and ν = 213 cm<sup>-1</sup> could be attributed to the vibration of GeSe bonds. The presence of the Raman peak at ν = 255 cm<sup>-1</sup> is due to the bond-stretching vibration of the disordered Se chains and rings. With the increase of the Ge concentration this peak shifts to a higher wavenumber due to the shortening of Se chains. The peak around ν = 300 cm<sup>-1</sup> is characteristic to Ge-Ge vibration mode. The Ge concentration slightly changes the shape of Micro-Raman spectra, mainly its ratio of the intensity.</p></dc:description> <dc:source>Proceedings of the Romanian Academy Series A - Mathematics Physics Technical Sciences Information Science () 545-550</dc:source> <dc:subject>chalcogenide glasses</dc:subject> <dc:subject>Coordination number</dc:subject> <dc:subject>Micro-</dc:subject> <dc:subject>Raman spectra</dc:subject> <dc:title>Micro-Raman spectra of bulk GexAsxSe1-2X chalcogenide glasses</dc:title> <dc:type>info:eu-repo/semantics/article</dc:type> </oai_dc:dc>
|
|
|