SM ISO690:2012 IASENIUC, Oxana, YOVU, M., GHIULNARE, A., MESTERCA, Raluca, JDERU, A., ENACHESCU, Marius. Micro-Raman spectra of bulk GexAsxSe1-2X chalcogenide glasses. In: Proceedings of the Romanian Academy Series A - Mathematics Physics Technical Sciences Information Science, 2018, vol. 19, pp. 545-550. ISSN 1454-9069. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Proceedings of the Romanian Academy Series A - Mathematics Physics Technical Sciences Information Science | ||||||
Volumul 19 / 2018 / ISSN 1454-9069 | ||||||
|
||||||
Pag. 545-550 | ||||||
|
||||||
Rezumat | ||||||
In this work are reported the Micro-Raman spectra of GexAsxSe1-2x (x = 0.05÷0.30). The Micro-Raman spectra consist of three main peaks located around ν = 193 cm-1, ν = 213 cm-1, and ν = 255 cm-1. The peaks around ν = 193 cm-1 and ν = 213 cm-1 could be attributed to the vibration of GeSe bonds. The presence of the Raman peak at ν = 255 cm-1 is due to the bond-stretching vibration of the disordered Se chains and rings. With the increase of the Ge concentration this peak shifts to a higher wavenumber due to the shortening of Se chains. The peak around ν = 300 cm-1 is characteristic to Ge-Ge vibration mode. The Ge concentration slightly changes the shape of Micro-Raman spectra, mainly its ratio of the intensity. |
||||||
Cuvinte-cheie chalcogenide glasses, Coordination number, Micro-, Raman spectra |
||||||
|
DataCite XML Export
<?xml version='1.0' encoding='utf-8'?> <resource xmlns:xsi='http://www.w3.org/2001/XMLSchema-instance' xmlns='http://datacite.org/schema/kernel-3' xsi:schemaLocation='http://datacite.org/schema/kernel-3 http://schema.datacite.org/meta/kernel-3/metadata.xsd'> <creators> <creator> <creatorName>Iaseniuc, O.V.</creatorName> <affiliation>Institutul de Fizică Aplicată, Moldova, Republica</affiliation> </creator> <creator> <creatorName>Iovu, M.S.</creatorName> <affiliation>Institutul de Fizică Aplicată, Moldova, Republica</affiliation> </creator> <creator> <creatorName>Ghiulnare, A.</creatorName> <affiliation>Universitatea Politehnică din Bucureşti, România</affiliation> </creator> <creator> <creatorName>Mesterca, R.</creatorName> <affiliation>Universitatea Politehnică din Bucureşti, România</affiliation> </creator> <creator> <creatorName>Jderu, A.</creatorName> <affiliation>Universitatea Politehnică din Bucureşti, România</affiliation> </creator> <creator> <creatorName>Enăchescu, M.</creatorName> <affiliation>Universitatea Politehnică din Bucureşti, România</affiliation> </creator> </creators> <titles> <title xml:lang='en'>Micro-Raman spectra of bulk GexAsxSe1-2X chalcogenide glasses</title> </titles> <publisher>Instrumentul Bibliometric National</publisher> <publicationYear>2018</publicationYear> <relatedIdentifier relatedIdentifierType='ISSN' relationType='IsPartOf'>1454-9069</relatedIdentifier> <subjects> <subject>chalcogenide glasses</subject> <subject>Coordination number</subject> <subject>Micro-</subject> <subject>Raman spectra</subject> </subjects> <dates> <date dateType='Issued'>2018-12-01</date> </dates> <resourceType resourceTypeGeneral='Text'>Journal article</resourceType> <descriptions> <description xml:lang='en' descriptionType='Abstract'><p>In this work are reported the Micro-Raman spectra of Ge<sub>x</sub>As<sub>x</sub>Se<sub>1-2x</sub> (x = 0.05÷0.30). The Micro-Raman spectra consist of three main peaks located around ν = 193 cm<sup>-1</sup>, ν = 213 cm<sup>-1</sup>, and ν = 255 cm<sup>-1</sup>. The peaks around ν = 193 cm<sup>-1</sup> and ν = 213 cm<sup>-1</sup> could be attributed to the vibration of GeSe bonds. The presence of the Raman peak at ν = 255 cm<sup>-1</sup> is due to the bond-stretching vibration of the disordered Se chains and rings. With the increase of the Ge concentration this peak shifts to a higher wavenumber due to the shortening of Se chains. The peak around ν = 300 cm<sup>-1</sup> is characteristic to Ge-Ge vibration mode. The Ge concentration slightly changes the shape of Micro-Raman spectra, mainly its ratio of the intensity.</p></description> </descriptions> <formats> <format>uri</format> </formats> </resource>