SM ISO690:2012 NIKOLAEVA, Albina, KONOPKO, Leonid, SHEPELEVICH, Vasily, PROKOSHIN, Valerii, GUSAKOVA, Sofia, BODYUL, P., POPOV, Ivan, GRIŢCO, Roman. Thermoelectric properties of Bi1-xSbx alloys, wires and foils. In: Nanotechnologies and Biomedical Engineering, Ed. 3, 23-26 septembrie 2015, Chișinău. Springer, 2015, Editia 3, p. 56. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Nanotechnologies and Biomedical Engineering Editia 3, 2015 |
|
Conferința "International Conference on Nanotechnologies and Biomedical Engineering" 3, Chișinău, Moldova, 23-26 septembrie 2015 | |
|
|
Pag. 56-56 | |
Rezumat | |
In this study we focus on characterization of the transport properties of Bi-10at%Sb wires with different diameters and Bi-9at%Sb foils, prepared by the high speed crystallization. The nanowires samples were cylindrical single- crystals with (1011) orientation along the wire axis and diameters from 300 nm to 3mkm. The rapidly solidified Bi-9at%Sb foils have a microcrystalline structure and texture (1012) and thickness 20-40 mkm. Electrical resistivity and thermoelectric power were measured in the temperature range 4.2-300 K on various wire diameters d. Here we show that the quantum confinement effect in semiconducting Bi0.9Sb0.1 nanowires increases the energy gap from 8.2 meV to 17.3 meV. When the diameter of nanowires is increased, the temperature range of exponential growth of resistance shifts into higher temperature region. The dependence of thermoelectric figure of merit on diameter of wires, foils structure and Sn- doping foil was calculated in a broad temperature interval. The results obtained may provide a new way of enhancing the figure of merit in a wide temperature range. |
|
|