SM ISO690:2012 HAJDEU-CHICAROS, Elena. Electrical properties of Cu2ZnGeS4 single crystals. In: Materials Science and Condensed Matter Physics, Ed. 7, 16-19 septembrie 2014, Chișinău. Chișinău, Republica Moldova: Institutul de Fizică Aplicată, 2014, Editia 7, p. 107. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Materials Science and Condensed Matter Physics Editia 7, 2014 |
|||||||
Conferința "Materials Science and Condensed Matter Physics" 7, Chișinău, Moldova, 16-19 septembrie 2014 | |||||||
|
|||||||
Pag. 107-107 | |||||||
|
|||||||
Descarcă PDF | |||||||
Rezumat | |||||||
The Cu2ZnGeS4 (CZGS) quatemaiy compound is promising for photovoltaic application as an absorber layer of low-cost thin film solar cells. It has a p-type of electrical conductivity and a high abso1ption coefficient [ 1]. Single c1ystals of CZGS were grown by chemical vapor transpo1t using iodine as a transpo1t agent. The temperature dependence of the resistivity p (111) in the range 10 - 300 K An activated character of conductivity was observed in all temperature range. The conductivity in the temperature range 200 - 300 K can be attributed to nearest neighbor hopping (NNH) type conductivity and/or to hole activation from defect acceptor level to the valence band mechanism. At the lower temperatures, 100 - 200 K, the Mott variable-range hopping (VRH) conductivity [2] was observed. Analysis of the Mott - VRH conductivity yields the value of the semi - width of the acceptor band, w~ 130 meV. From the rectangular shape approximation of the density of the states for an acceptor band, the values of the relative acceptor concentration NINc~ 0.2 and the localization radius a/ao ~ 1.2 can be obtained. The values yielded that the investigated samples of CZGS ai·e far from the metal - insulator transition. |
|||||||
|
Cerif XML Export
<?xml version='1.0' encoding='utf-8'?> <CERIF xmlns='urn:xmlns:org:eurocris:cerif-1.5-1' xsi:schemaLocation='urn:xmlns:org:eurocris:cerif-1.5-1 http://www.eurocris.org/Uploads/Web%20pages/CERIF-1.5/CERIF_1.5_1.xsd' xmlns:xsi='http://www.w3.org/2001/XMLSchema-instance' release='1.5' date='2012-10-07' sourceDatabase='Output Profile'> <cfResPubl> <cfResPublId>ibn-ResPubl-72990</cfResPublId> <cfResPublDate>2014</cfResPublDate> <cfVol>Editia 7</cfVol> <cfStartPage>107</cfStartPage> <cfISBN></cfISBN> <cfURI>https://ibn.idsi.md/ro/vizualizare_articol/72990</cfURI> <cfTitle cfLangCode='EN' cfTrans='o'>Electrical properties of Cu2ZnGeS4 single crystals</cfTitle> <cfAbstr cfLangCode='EN' cfTrans='o'><p>The Cu2ZnGeS4 (CZGS) quatemaiy compound is promising for photovoltaic application as an absorber layer of low-cost thin film solar cells. It has a p-type of electrical conductivity and a high abso1ption coefficient [ 1]. Single c1ystals of CZGS were grown by chemical vapor transpo1t using iodine as a transpo1t agent. The temperature dependence of the resistivity p (111) in the range 10 - 300 K An activated character of conductivity was observed in all temperature range. The conductivity in the temperature range 200 - 300 K can be attributed to nearest neighbor hopping (NNH) type conductivity and/or to hole activation from defect acceptor level to the valence band mechanism. At the lower temperatures, 100 - 200 K, the Mott variable-range hopping (VRH) conductivity [2] was observed. Analysis of the Mott - VRH conductivity yields the value of the semi - width of the acceptor band, w~ 130 meV. From the rectangular shape approximation of the density of the states for an acceptor band, the values of the relative acceptor concentration NINc~ 0.2 and the localization radius a/a<sub>o</sub> ~ 1.2 can be obtained. The values yielded that the investigated samples of CZGS ai·e far from the metal - insulator transition.</p></cfAbstr> <cfResPubl_Class> <cfClassId>eda2d9e9-34c5-11e1-b86c-0800200c9a66</cfClassId> <cfClassSchemeId>759af938-34ae-11e1-b86c-0800200c9a66</cfClassSchemeId> <cfStartDate>2014T24:00:00</cfStartDate> </cfResPubl_Class> <cfResPubl_Class> <cfClassId>e601872f-4b7e-4d88-929f-7df027b226c9</cfClassId> <cfClassSchemeId>40e90e2f-446d-460a-98e5-5dce57550c48</cfClassSchemeId> <cfStartDate>2014T24:00:00</cfStartDate> </cfResPubl_Class> <cfPers_ResPubl> <cfPersId>ibn-person-32461</cfPersId> <cfClassId>49815870-1cfe-11e1-8bc2-0800200c9a66</cfClassId> <cfClassSchemeId>b7135ad0-1d00-11e1-8bc2-0800200c9a66</cfClassSchemeId> <cfStartDate>2014T24:00:00</cfStartDate> </cfPers_ResPubl> </cfResPubl> <cfPers> <cfPersId>ibn-Pers-32461</cfPersId> <cfPersName_Pers> <cfPersNameId>ibn-PersName-32461-3</cfPersNameId> <cfClassId>55f90543-d631-42eb-8d47-d8d9266cbb26</cfClassId> <cfClassSchemeId>7375609d-cfa6-45ce-a803-75de69abe21f</cfClassSchemeId> <cfStartDate>2014T24:00:00</cfStartDate> <cfFamilyNames>Hajdeu-Chicaros</cfFamilyNames> <cfFirstNames>Elena</cfFirstNames> </cfPersName_Pers> </cfPers> </CERIF>