The results of investigation of the surface structure-phase transformation of the iron specimens subjected carbonization by the electrosparking method and heating in the temperature range 20-800oC are given. It is sound that after electrosparking alloying with graphite the surface layer consisting of main austenite and cementite forms with high carbon content in γ-Fe. The austenite quantity reduces with heating and at 300oC it fully turns into ferrite-cementite mixture (perlite). The specimens heating reduces the value of microstresses, diffraction lines narrow down coming nearer to the annealed armco-iron values. |
||||||
|
Dublin Core Export
<?xml version='1.0' encoding='utf-8'?> <oai_dc:dc xmlns:dc='http://purl.org/dc/elements/1.1/' xmlns:oai_dc='http://www.openarchives.org/OAI/2.0/oai_dc/' xmlns:xsi='http://www.w3.org/2001/XMLSchema-instance' xsi:schemaLocation='http://www.openarchives.org/OAI/2.0/oai_dc/ http://www.openarchives.org/OAI/2.0/oai_dc.xsd'> <dc:creator>Mihailiuc, A.I.</dc:creator> <dc:creator>Volodina, G.F.</dc:creator> <dc:date>2010-12-22</dc:date> <dc:description xml:lang='ru'>The results of investigation of the surface structure-phase transformation of the iron specimens subjected carbonization by the electrosparking method and heating in the temperature range 20-800oC are given. It is sound that after electrosparking alloying with graphite the surface layer consisting of main austenite and cementite forms with high carbon content in γ-Fe. The austenite quantity reduces with heating and at 300oC it fully turns into ferrite-cementite mixture (perlite). The specimens heating reduces the value of microstresses, diffraction lines narrow down coming nearer to the annealed armco-iron values. </dc:description> <dc:source>Электронная обработка материалов 46 (6) 53-55</dc:source> <dc:title>Структурно-фазовые изменения в электроискровых железоуглеродистых покрытиях при различных температурах их нагрева</dc:title> <dc:type>info:eu-repo/semantics/article</dc:type> </oai_dc:dc>