In recent years different types of titanium alloys have been investigated with the aim of utilizing materials in biomaterials field, and Ti–Zr system alloys are very promising materials. In this paper, microstructure and morphology of ZrO2-CaO coating deposited on Ti-55Zr alloy is investigated. Zirconia ceramic coating was deposited using Sulzer Metco 9MCE atmospheric plasma spraying, in order to improve corrosion resistance and biocompatibility. Microstructure and phase analysis of based material and ceramic coating were investigated using scanning electron microscopy, X-ray diffractometry (XRD). The coated layer presents a homogenous aspect with an average thickness layer of 120 microns and some small cracks and splats.

În ultimii ani diferite tipuri de aliaje de titan au fost analizate în scopul utilizării lor în aplicaţiile biomedicale, sub diverse forme de proteze şi implanturi. În această lucrare au fost analziate microstructura şi morfologia stratului de ZrO2-CaO depus pe un aliaj Ti-55Zr. Acoperirea ceramică de zirconiu a fost realizată utilizând o instalaţie de depunere în jet de plasmă Sulzer Metco 9MCE, în scopul îmbunătăţirii rezistenţei la coroziune şi a biocompatibilităţii. Microstructura şi analiza de faze a materialului de baza şi stratului ceramic depus au fost efectuate utilizând microscopia cu scanare de electroni şi difracţia de raze X. Stratul depus a prezentat un aspect omogen cu o grosime medie a stratului de 120 microni şi cu prezenţa unor “splat-uri” şi mici fisuri.