Chromium obtaining from armenian chromite concentrates by SHS in the presence of chlorides
Închide
Conţinutul numărului revistei
Articolul precedent
Articolul urmator
1255 10
Ultima descărcare din IBN:
2023-06-14 10:29
SM ISO690:2012
MARTIROSYAN, V., TOROSYAN, Gagik, TOROSYAN, N., SASUNTSYAN, M.. Chromium obtaining from armenian chromite concentrates by SHS in the presence of chlorides . In: Meridian Ingineresc, 2012, nr. 2, pp. 33-37. ISSN 1683-853X.
EXPORT metadate:
Google Scholar
Crossref
CERIF

DataCite
Dublin Core
Meridian Ingineresc
Numărul 2 / 2012 / ISSN 1683-853X

Chromium obtaining from armenian chromite concentrates by SHS in the presence of chlorides

Pag. 33-37

Martirosyan V., Torosyan Gagik, Sasuntsyan M., Torosyan N.
 
State Engineering University of Armenia
 
Disponibil în IBN: 11 decembrie 2013


Rezumat

A fost elaborată tehnologia metalurgică inovatoare de procesare complexă a cromiţilor din Sevan pentru producerea de crom metalic în regim SHS. În acest scop, s-a investigat procesul de creştere a reactivităţii concentratelor de cromit (pentru conţinutul de 53% Cr2O3), ca urmare a tratamentului termic şi mecano - chimic, atât în prezenţa cât şi în absenţă de clorură. S-a arătat că, în ambele cazuri, atât la încălzire, cât şi la mărunţire, în prezenţa de cloruri are loc clorurarea selectivă similară clorurării de înaltă temperatură formînduse clorură de fier şi clorură de magneziu, după spălarea şi uscarea cărora sunt obţinute superconcentrate care conţin Cr2O3 - 74,12, în caz de revenire, şi 77.23 %, în cazul activării mecanice, cu un conţinut scăzut de fier şi de magneziu. Este indicată posibilitatea de a produce crom metalic, cu un conţinut scăzut de fier şi de magneziu prin procesarea superconcentratului obţinut, prin metoda aluminotermică de recuperare.

We developed an innovative technology for processing metal complex chromites Sevan to produce chromium metal in SHS regime. In this case, we studied the increased reactivity of chromite concentrates (for the content of 53% Cr2O3), due to thermal and mechanical - chemical treatment, both in the presence and in the absence of chloride. It was shown that in both cases, both the heating and grinding, in the presence of chlorides the selective chlorination takes place similar high temperature chlorination in obtaining of iron chloride and magnesium chloride. After washing and drying are obtained superconcentrates containing Cr2O3 - 74.12, in case of return, and 77.23% for the mechanical activation, with a low iron and magnesium. It was suggested the possibility of producing metallic chromium with a low content of iron and magnesium, for the treatment of superconcentrat obtained by the aluminothermic method of recovery.

On a développé une technologie métallique innovante pour le traitement complexe des chromites de Sevan pour produire du métal de chrome dans régime SHS. À cette fin, nous avons étudié l'augmentation de la réactivité de la chromite concentrés (pour le contenu de 53% Cr2O3), due à un traitement thermique et mécanique - chimique, à la fois aujourd'hui et dans l'absence de chlorure. On a montré que dans les deux cas, à la fois le chauffage, ainsi que le broyage, en présence de chlorures a lieu la chloration sélective similaire a la chloration dans haute température en obtenant du chlorure de fer et du chlorure de magnésium, après le lavage et le séchage desquels sont obtenus superconcentrés contenant Cr2O3 - 74.12, en cas de retour, et 77,23% pour l'activation mécanique, avec une faible teneur en fer et en magnésium. On a indiqué la possibilité de produire du chrome métallique avec un faible contenu du fer et du magnésium, par le traitement de superconcentrat obtenue par la méthode aluminothermique de récupération.

Разработана нетрадиционная металлургическая технология комплексной переработки севанских хромитов с получением металлического хрома в режиме СВС. С этой целью исследован процесс увеличения реакционной способности хромитовых концентратов (при содержании 53 % Cr2O3), в результате термической и механохимической обработки, как в присутствии, так и в отсутствие хлоридов. Выявлено, что в обоих случаях как при нагревании, так и при измельчении в присутствии хлоридов происходит селективное хлорирование аналогично высокотемпературному хлорированию и образуются хлориды железа и магния, промыванием и просушиванием которых получается суперконцентрат с содержанием Cr2O3 – 74,12 в случае отжига и 77,23%, в случае механохимической активации, с низким содержанием железа и магния. Показана возможность получения металлического хрома с низким содержанием железа и магния путем переработки полученного суперконцентрата внепечным, алюминотермическим способом восстановления.