Combustion synthesis and characterization of nanosized powder SrAl2O4:Eu2+ phosphor
Închide
Conţinutul numărului revistei
Articolul precedent
Articolul urmator
986 3
Ultima descărcare din IBN:
2021-04-07 18:38
SM ISO690:2012
CALYN, S., NAZAROV, Michael V., NAZIDA, AwangNor, AHMAD-FAUZI, M.. Combustion synthesis and characterization of nanosized powder SrAl2O4:Eu2+ phosphor. In: Moldavian Journal of the Physical Sciences, 2012, nr. 1-2(11), pp. 112-123. ISSN 1810-648X.
EXPORT metadate:
Google Scholar
Crossref
CERIF

DataCite
Dublin Core
Moldavian Journal of the Physical Sciences
Numărul 1-2(11) / 2012 / ISSN 1810-648X /ISSNe 2537-6365

Combustion synthesis and characterization of nanosized powder SrAl2O4:Eu2+ phosphor

Pag. 112-123

Calyn S.1, Nazarov Michael V.21, Nazida AwangNor1, Ahmad-Fauzi M.1
 
1 School of Materials and Mineral Resources Engineering, University Sains Malaysia,
2 Institute of Applied Physics, Academy of Sciences of Moldova
 
Disponibil în IBN: 16 decembrie 2013


Rezumat

A stoichiometric SrAl2O4:Eu2 nanosized powder was synthesized by combustion synthesis using urea at 500°C. The crystal structure, element and phase composition, and particle size were analyzed with the aim to study the properties of nanosized SrAl2O4:Eu2 green phosphor and its application. X-ray Diffraction pattern revealed that the SrAl2O4:Eu2 crystallizes were a major phase, and Sr4Al14O25 as a secondary phase with a small amount of the dopant has no effect on the crystal structure of SrAl2O4. Crystalline structure can be observed and enhanced by calcination at 1000ºC with 2-h soaking time in a reductive atmosphere. Nucleation of particles occurs and forms a needle-like structure for SrAl2O4 and a star-like structure for SrAl2O4:Eu2 . This structure is unstable and agglomerates during calcination at 1000 °C to form a stable specific flower-like structure which enhances the glowing effect of the samples.