SM ISO690:2012 KOLIBABA, Gleb, COSTRIUCOVA, Natalia, RUSNAC, Dumitru, BUSUIOC, Simon, MONAICO, Eduard. Wettability of Highly Conductive ZnO:Ga:Cl CVT Ceramics with Various Ga Content. In: Nanotechnologies and Biomedical Engineering, Ed. 5, 3-5 noiembrie 2021, Chişinău. Chişinău: Pontos, 2021, Ediția 5, p. 114. ISBN 978-9975-72-592-7. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Nanotechnologies and Biomedical Engineering Ediția 5, 2021 |
|||||
Conferința "Nanotechnologies and Biomedical Engineering" 5, Chişinău, Moldova, 3-5 noiembrie 2021 | |||||
|
|||||
Pag. 114-114 | |||||
|
|||||
Descarcă PDF | |||||
Rezumat | |||||
ZnO:Ga:Cl ceramics were sintered using chemical vapor transport technique. Ga content was varied in a range of 0 10 mol %. The wettability of unpolished and polished surface of ZnO:Ga:Cl ceramics was investigated. The polished and etched surface of ZnO ceramics is in a hydrophilic state. The presence of Ga impurity leads to a strong increase in the water contact angle to 131. This behavior is attributed to a high concentration of free electrons, which suppress the formation of intrinsic surface defects acting as traps for water molecules. Air pockets on unpolished surfaces of ZnO:Ga:Cl ceramics are an additional factor that increases the water contact angle. |
|||||
|