The durability of insulation systems for pipelines is determined by the operational resistance of the pipeline material and the design of the insulation system. The issue of studying the corrosion processes of steel pipelines under various heat-insulating materials is relevant. The aim of the work was to study the process of corrosion of steel pipelines under insulating materials of various nature and porosity. The object of research is pipeline insulation systems. The subject of research is the corrosion processes in various insulation systems. This goal was achieved by carrying out a set of experimental studies aimed at studying the rate of the corrosion process of the metal of the pipeline, insulated with various materials, with the subsequent calculation of the remaining service life of the pipeline. The most significant results are: the dependence of the corrosion rate and the area of damage of carbon steel on the structure (porosity) of the heat-insulating material, the residual number of ions of water-soluble chlorides. It was found that the maximum corrosion rate of steel under materials with open porosity is 0.29-0.41 mm/year. The increase in the rate of the corrosion process is directly proportional to the increase in the number of chlorine anions in the structure of the material. The smallest area of corrosion damage to the steel surface is observed under materials with open porosity. The significance of the results obtained consists in determining the residual life of the pipeline under a heat-insulating layer of various materials.

Scopul lucrării constă în studierea procesului de coroziune a conductelor de oțel de alimentare cu apă caldă sub materiale izolatoare de diferite natură și porozitate. Obiectul cercetării îl constituie sistemele de izolare a conductelor. Subiectul cercetării îl constituie procesele de coroziune ale conductelor de apă caldă din diferite sisteme de izolație. Acest obiectiv a fost atins prin efectuarea unui set de studii experimentale menite să studieze viteza procesului de coroziune a metalului conductei, izolat cu diverse materiale, cu calcularea ulterioară a duratei de viață rămase a conductei. Cele mai semnificative rezultate sunt: dependența vitezei de coroziune și zona de deteriorare a oțelului carbon de structura (porozitatea) materialului termoizolant, numărul rezidual de ioni de cloruri solubile în apă. S-a constatat că viteza maximă de coroziune a oțelului sub materiale cu porozitate deschisă este de 0,29-0,41 mm / an, care este de 1,8-2,7 ori mai mică decât în cazul materialelor cu porozitate închisă. Creșterea ratei procesului de coroziune este direct proporțională cu creșterea numărului de anioni de clor din structura materialului. Cea mai mică zonă de deteriorare a coroziunii la suprafața oțelului se observă la materialele cu porozitate deschisă. Semnificația rezultatelor obținute constă în determinarea duratei de viață reziduală a conductei sub stratul termoizolant din diverse materiale și stabilirea tipurilor de materiale termoizolante, în aplicarea cărora coroziunea sub izolație se desfășoară la cea mai mică rată. Dintre materialele utilizate în sistemele de izolație, cele mai bune rezultate au fost obținute pentru produsele din lână minerală din lână de piatră cu un număr redus de cloruri

Долговечность систем изоляции хозяйственных объектов, в том числе трубопроводов, определяется эксплуатационной стойкостью материала трубопровода и конструкцией изоляционной системы. Известно, что пористость, проницаемость и состав материала изоляционной системы оказывают определенное влияние на коррозионный процесс трубопровода. Коррозия под изоляцией является общепризнанной проблемой. Вопрос исследования коррозионных процессов стальных трубопроводов под различными теплоизоляционными материалами является актуальным. Целью работы явилось исследование процесса коррозии стальных трубопроводов горячего водоснабжения под изоляционными материалами различной природы и пористости. Объект исследования – системы изоляции трубопроводов. Предмет исследования – коррозионные процессы трубопроводов горячего водоснабжения в различных системах изоляции. Поставленная цель достигнута путём проведения комплекса экспериментальных исследований, направленных на изучение скорости коррозионного процесса металла трубопровода, изолированного различными материалами, с последующим расчетом остаточного срока службы трубопровода. Наиболее существенными результатами являются: зависимости скорости коррозии и площади повреждения углеродистой стали от структуры (пористости) теплоизоляционного материала, остаточного числа ионов водорастворимых хлоридов. Установлено, что максимальная скорость коррозии стали под материалами с открытой пористостью составляет 0,29-0,41 мм/год, что в 1,8–2,7 раза ниже, чем под материалами с закрытой пористостью. Увеличение скорости коррозионного процесса прямо пропорционально увеличению числа анионов хлора в структуре материала. Наименьшая площадь коррозионного повреждения поверхности стали наблюдается под материалами с открытой пористостью. Значимость полученных результатов состоит в определении остаточного срока службы трубопровода под теплоизоляционным слоем из различных материалов и установлении типов теплоизоляционных материалов, при применении которых коррозия под изоляцией протекает с наименьшей скоростью. Из применяемых в системах изоляции материалов лучшие результаты получены для минераловолокнистых изделий из каменной ваты с пониженным числом содержания хлоридов