Single-phase SrAl₂O₄:Eu²⁺ and multiphase {SrAl2O4+Sr4Al14O25}:Eu2+ phosphors, as well as those codoped additionally with Dy3+, are prepared by solid state reaction and combustion synthesis. The codoping of SrAl2O4:Eu2+ with Dy3+ leads to an increase in the afterglow duration from a few minutes up to many hours and makes the afterglow much brighter, which is important in some applications. It is shown that the emission band of the phosphors can be shifted from green to blue-green spectral range by changing the synthesis method. Composite color cathodoluminescence and photoluminescent analysis are applied to control the synthesis process. The presence of different emission centers and their distribution in the studied phosphors is shown. Some of their numerous applications, such as display devices, painting, and biological applications, are shown.

Luminoforii monofazici SrAl2O4:Eu2+ și luminoforii multifazici {SrAl2O4+Sr4Al14O25}:Eu2+, precum și cei dopați suplimentar cu Dy3+, au fost obținuți prin reacție în fază solidă și sinteză prin combustie. Datorită dopării suplimentare a SrAl2O4:Eu2+ cu Dy3+, postluminescența a crescut de la câteva minute la multe ore și a devenit mult mai luminoasă, ceea ce este important în unele aplicații. Se arată că banda de emisie a luminoforilor poate fi deplasată de la spectrul verde la cel albastru-verde prin schimbarea metodei de sinteză. Pentru a controla procesul de sinteză, s-au aplicat catodoluminiscența color și analiza fotoluminiscenței. Se demonstrează prezența diferitelor centre de radiație și distribuția lor în luminoforii investigați. Sunt prezentate unele dintre numeroasele domenii de aplicații, cum ar fi, dispositive de afișare, pictură și biologie.