The paper presents a study on the corrosion processes in reinforced concrete construction elements operated in harsh environments, which may influence the stability of the building. In the experimental program were tried and nefisurate prefisurate evidence in the form of beams, the service limit state (SLS) after accelerated corrosion tests in solutions of Na2SO4 and NaCl. Election quick schemes testing corrosive mechanism respected the processes occurring on the surface of reinforcement under natural conditions. Due to accelerated corrosion exposure prefisurate beams in Na2SO4 and NaCl solutions, the yield strength is 7% lower than the corresponding standard beams exposed to accelerated corrosion in gullies service limit state (SLS). The tested beams have shown good results at external influences that allows to carry out the further researches, is especial at studying influence of duration of the accelerated influence of the corrosion environment, potential of a current and other diameters of armatures

În articol se prezintă un studiu privind procesele de coroziune a elementelor de construcţii din beton armat, exploatate în medii agresive, care pot influenţa stabilitatea construcţiilor. În baza programului experimental s-au încercat probe prefisurate şi nefisurate, sub forme de grinzi, la stadiul limită de serviciu (SLS), după testări la coroziune accelerată în soluţii de Na2SO4 şi NaCl. Alegerea regimurilor de testare corosivă rapide s-a făcut cu respectarea mecanismului proceselor care au loc pe suprafaţa armăturii în condiţii naturale. Datorită expunerii la coroziune accelerată a grinzilor prefisurate, în soluţii de Na2SO4 şi NaCl, valoarea forţei de cedare este cu 7 % mai mică, decât cea corespunzătoare grinzilor etalon, expuse la coroziune accelerată fără fisuri în stadiul limită de serviciu (SLS). Grinzile testate au demonstrat o comportare bună la acţiunea solicitărilor exterioare, încurajând studii viitoare asupra subiectului, cu precădere la studiul influenţei timpului de expunere la coroziune accelerată, intensităţii curentului aplicat şi al altor diametre de armături.

В статье представлено исследование процессов коррозии железобетонных элементов конструкций, эксплуатируемых в агрессивных средах, которые могут повлиять на устойчивость конструкций. На основании экспериментальной программы были испытаны пробы в виде балок с трещинами и без, на несущую способность, после ускоренных коррозионных испытаний в растворах Na2SO4 и NaCl. Выбор режимов коррозионных испытаний проводился с соблюдением механизмов процессов, которые проходят на поверхности арматуры, в естественных условиях. В результате ускореных коррозионных испытаний балок с трещинами, в растворах Na2SO4 и NaCl, значение усилия разрушения на 7 % ниже, чем соответствующее значение балок эталон, подверженые ускоренному коррозионному испытанию, без трещин при крайних стадиях работы. Испытанные балки показали хорошие результаты при внешних воздействиях, что позволяет провести дальнейшие исследования, особенно при изучении влияния продолжительности ускоренного воздействия коррозионной среды, потенциала тока и других диаметров арматур.