 SM ISO690:2012TSYNTSARU, Natalia, KAVAS, Berkay, CELIS, Jean-Pierre. Synthesis of AAO nanotemplate and its properties. In: Nanotechnologies and Biomedical Engineering, Ed. 1, 7-8 iulie 2011, Chișinău. Technical University of Moldova, 2011, Editia 1, pp. 75-79. ISBN 978-9975-66-239-0.. |
| EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
| Nanotechnologies and Biomedical Engineering Editia 1, 2011 |
||||||
|
Conferința "International Conference on Nanotechnologies and Biomedical Engineering" 1, Chișinău, Moldova, 7-8 iulie 2011 | ||||||
|
||||||
| Pag. 75-79 | ||||||
|
||||||
 Descarcă PDF |
||||||
| Rezumat | ||||||
The objective of this study is to synthesize and to characterize anodized aluminium oxide (AAO) nano-templates suited for large area device applications. The wear performance and the mechanical properties of well-ordered nanoporous AAO obtained after a two step anodizing process in sulphuric acid were investigated. Pores with different aspect ratios were obtained at cell voltages of 15 V and 21V. Ppore diameters of ~16 nm and ~ 27 nm were noticed. The mechanical behaviour of such anodized aluminium oxides (AAO) was determined by nanoindentation at 2 -200mN normal loads. The tribological behaviour of these nano-templates was studied under reciprocating (ball on flat) sliding against alumina counter-balls. The dependence of the properties of AAO-templates on the small pore diameter is discussed |
||||||
| Cuvinte-cheie anodized aluminium oxide, friction and wear, hardness, pore diameter |
||||||
|
|
|
|