Photoconductivity spectra of amorphous multilayer structures
Close
Articolul precedent
Articolul urmator
458 0
SM ISO690:2012
IASENIUC, Oxana, YOVU, M.. Photoconductivity spectra of amorphous multilayer structures. In: Proceedings of SPIE - The International Society for Optical Engineering, 20-23 august 2020, Constanta. Bellingham, USA: SPIE, 2020, Vol.11718, p. 0. ISBN 978-151064271-3. ISSN 0277786X. DOI: https://doi.org/10.1117/12.2571100
EXPORT metadate:
Google Scholar
Crossref
CERIF

DataCite
Dublin Core
Proceedings of SPIE - The International Society for Optical Engineering
Vol.11718, 2020
Conferința "Advanced Topics in Optoelectronics, Microelectronics and Nanotechnologies X 2020"
Constanta, Romania, 20-23 august 2020

Photoconductivity spectra of amorphous multilayer structures

DOI: https://doi.org/10.1117/12.2571100

Pag. 0-0

Iaseniuc Oxana, Yovu M.
 
Institute of Applied Physics
 
Disponibil în IBN: 27 ianuarie 2021


Rezumat

Amorphous thin films of chalcogenide glasses are well known as high photosensitive materials with a wide application in photonics, optoelectronics and information storage systems. In the present paper the experimental results on optical absorption and steady-state photocurrent of amorphous single amorphous layer structures Al-Ge0.30As0.04S0.66-Al (L1) AlGe0.09As0.09Se0.82-Al (L2), Al-As0.40S0.30Se0.30-Al (L3) as well as for amorphous heterostructure AlAs0.40S0.30Se0.30/Ge0.09As0.09Se0.82/Ge0.30As0.04S0.66-Al (HS) at different values of the applied voltage at positive and negative polarity of the illuminated top Al electrode are presented and discussed. The thickness of the component layers is also different with the ratio of the thickness about L1/L2/L3 = 1000/500/200 nm. The investigated multilayer structures contain the first material with the trigonal (As0.40S0.30Se0.30), and the other two layers contain trigonal as well as tetrahedral structural units (Ge0.09As0.09Se0.82, Ge0.30As0.04S0.66). The complex structure of the photocurrent spectra is governed to the different value of the optical band gap of the involved amorphous layer (about Eg∼2.0 eV for the As0.40S0.30Se0.30 and Ge0.09As0.09Se0.82, and about Eg∼3.0 eV for the Ge0.30As0.04S0.66). The obtained experimental results are discussed taking into account the depth of the light absorption depending of the nature and the thickness of each amorphous material, wavelength and the contact phenomena between the interfaces of the different material as well as between the interfaces metal-amorphous semiconductor with different work functions, as was demonstrated for the other amorphous thin film structures.



Cuvinte-cheie
amorphous multilayer structures, Photocurrent., transmission spectra